Analysis of the formation mechanism of TiC particles produced by in situ reaction in molten aluminum
文献类型:期刊论文
作者 | Yang, B; Wang, YQ; Zhang, J; Zhou, BL |
刊名 | RARE METAL MATERIALS AND ENGINEERING
![]() |
出版日期 | 1997-12-01 |
卷号 | 26期号:6页码:12-17 |
关键词 | TiC/Al composite in situ reaction TiC particulate formation mechanism |
ISSN号 | 1002-185X |
通讯作者 | Yang, B() |
英文摘要 | The formation mechanism to TiC particles formed by in situ reaction in molten aluminum is studied by means of XRD, EPMA, TEM and SEM techniques in this paper. The results reveal that (1) the heat liberated by the reaction 3Al((1))+Ti-(s)-->Al3Ti can ignite the reaction Ti+C-->TiC; (2)diffusion or/and solution-precipitation mechanisms, two well-known mechanisms of TiC particle formation in Self-propagating High-temperature Synthesis(SHS), are thought to be in operation. At lower temperatures, the reaction leading to TiC particle formation is controlled by a diffusion mechanism of relatively slower velocity. In this regime, the aluminum powders melt with increasing temperature of the preform, thereby igniting TiC particle reaction. At the higher temperatures, the reaction Ti+C-->TiC is controlled by the solution-precipitation mechanism, i.e. the diffusion and solution-precipitation mechanisms are both present in this regime. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
WOS记录号 | WOS:000071445800003 |
出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
源URL | [http://ir.imr.ac.cn/handle/321006/107521] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Yang, B |
作者单位 | 1.Acad Sinica, Inst Met Res, Shenyang 110015, Peoples R China 2.Nanchang Univ, Nanchang 330029, Peoples R China 3.Acad Sinica, Int Ctr Mat Phys, Shenyang 110015, Peoples R China |
推荐引用方式 GB/T 7714 | Yang, B,Wang, YQ,Zhang, J,et al. Analysis of the formation mechanism of TiC particles produced by in situ reaction in molten aluminum[J]. RARE METAL MATERIALS AND ENGINEERING,1997,26(6):12-17. |
APA | Yang, B,Wang, YQ,Zhang, J,&Zhou, BL.(1997).Analysis of the formation mechanism of TiC particles produced by in situ reaction in molten aluminum.RARE METAL MATERIALS AND ENGINEERING,26(6),12-17. |
MLA | Yang, B,et al."Analysis of the formation mechanism of TiC particles produced by in situ reaction in molten aluminum".RARE METAL MATERIALS AND ENGINEERING 26.6(1997):12-17. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。