Effect of HCl on the corrosion and wear of in-bed tubes in a laboratory simulated bubbling fluidized bed
文献类型：期刊论文
| 作者 | Hou, PY; Niu, Y; Sum, TJ; Stringer, J |
| 刊名 | WEAR
 |
| 出版日期 | 1999-12-01 |
| 卷号 | 233页码:635-646 |
| 关键词 | corrosion wear in-bed tube |
| ISSN号 | 0043-1648 |
| 通讯作者 | Hou, PY() |
| 英文摘要 | Heat-exchanger tubes in fluidized bed combustors (FBCs) often suffer material loss due to combined corrosion and erosion. The effect of chlorine on in-bed tube wastage and its possible mechanism are being studied using the EPRI/LBNL FBC wastage simulator. This test rig was designed to simulate dense particle impacts on tube bottoms with well-controlled parameters, and has been proven to closely reflect situations found in operating bubbling FBCs, In this study, HCl gas was chosen to be the Cl source and was introduced into the fluidizing air with a 50-ppm concentration. Tests were performed at temperatures ranging from ambient to 400 degrees C using 1018 low carbon steel rods in a bed of commercial SiO(2) sand that had an average size of 800 mu m. The wear profile after each test was measured using a profilometer. Results showed an increase in material wastage rates in the presence of HCl, and that the rate was significantly higher with higher test temperatures. Microstructural and chemical analysis of the wear surface and corrosion products are reported. It is concluded that the dominating effect of HCl on the wastage rates is due to an enhanced oxidation and a reduced scale adherence. (C) 1999 Elsevier Science S.A. AU rights reserved. |
| WOS研究方向 | Engineering ; Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:000084590500070 |
| 出版者 | ELSEVIER SCIENCE SA |
| 源URL | [http://ir.imr.ac.cn/handle/321006/109047]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Hou, PY |
| 作者单位 | 1.Lawrence Berkeley Natl Lab, Div Mat Sci, Berkeley, CA 94720 USA 2.Chinese Acad Sci, Inst Corros & Protect Met, Shenyang, Peoples R China 3.Elect Power Res Inst, Palo Alto, CA 94304 USA |
| 推荐引用方式 GB/T 7714 | Hou, PY,Niu, Y,Sum, TJ,et al. Effect of HCl on the corrosion and wear of in-bed tubes in a laboratory simulated bubbling fluidized bed[J]. WEAR,1999,233:635-646. |
| APA | Hou, PY,Niu, Y,Sum, TJ,&Stringer, J.(1999).Effect of HCl on the corrosion and wear of in-bed tubes in a laboratory simulated bubbling fluidized bed.WEAR,233,635-646. |
| MLA | Hou, PY,et al."Effect of HCl on the corrosion and wear of in-bed tubes in a laboratory simulated bubbling fluidized bed".WEAR 233(1999):635-646. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。