Compression fracture of bulk Zr55Al10Ni5Cu30 amorphous alloy at high temperature
文献类型：期刊论文
| 作者 | Zhang, QS; Zhang, HF; Wang, AM; Ding, BZ; Hu, ZQ |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2002-08-01 |
| 卷号 | 38期号:8页码:835-838 |
| 关键词 | bulk Zr55Al10Ni5Cu30 amorphous alloy high temperature compression fracture fracture surface adiabatic heating |
| ISSN号 | 0412-1961 |
| 通讯作者 | Zhang, QS() |
| 英文摘要 | The fracture behavior of bulk Zr55Al10Ni5Cu30 amorphous alloy under uniaxial compression at high temperature has been investigated. At room temperature, a crack with serrated edge appeared on the ridge of veins at the fracture surface for the bulk Zr55Al10Ni5Cu30 amorphous alloy. At high temperature, the compressive fracture surface of bulk Zr55Al10Ni5Cu30 amorphous alloy became much rougher than that at room temperature, and steps appeared on the fracture surface. With increasing the temperature, a different pattern from the vein appeared on the fracture surface at high temperature, which is very similar to the flowing-liquid solidified immediately. This type of fracture is most likely due to the adiabatic heating created by plastic flow. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000177977000010 |
| 出版者 | SCIENCE CHINA PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/114324]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zhang, QS |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, QS,Zhang, HF,Wang, AM,et al. Compression fracture of bulk Zr55Al10Ni5Cu30 amorphous alloy at high temperature[J]. ACTA METALLURGICA SINICA,2002,38(8):835-838. |
| APA | Zhang, QS,Zhang, HF,Wang, AM,Ding, BZ,&Hu, ZQ.(2002).Compression fracture of bulk Zr55Al10Ni5Cu30 amorphous alloy at high temperature.ACTA METALLURGICA SINICA,38(8),835-838. |
| MLA | Zhang, QS,et al."Compression fracture of bulk Zr55Al10Ni5Cu30 amorphous alloy at high temperature".ACTA METALLURGICA SINICA 38.8(2002):835-838. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。