Corrosion behavior of K38G alloy and its nanocrystalline coating in molten sulfate at 900 degrees C
文献类型：期刊论文
| 作者 | Geng, SJ; Wang, FH; Zhu, SL |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2002-08-01 |
| 卷号 | 38期号:8页码:871-876 |
| 关键词 | K38G alloy sputtering nanocrystalline coating molten sulfate hot corrosion |
| ISSN号 | 0412-1961 |
| 通讯作者 | Geng, SJ() |
| 英文摘要 | A nanocrystalline coating with the same composition as K38G alloy was sputtered on the substrate alloy K38G by means of magnetron sputtering method. The corrosion behaviors of cast alloy and its sputtered nanocrystalline coating in molten 75Na(2)SO(4)+25%K2SO4 at 900 degreesC were studied. The results indicate that the coating prolonged the incubation of the breakaway corrosion and improved the hot corrosion resistance of K38G alloy due to the formation of a continuous and compact Al2O3 scale on it. The hot corrosion mechanisms of the cast alloy and the coating were discussed. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000177977000018 |
| 出版者 | SCIENCE CHINA PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/115103]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Geng, SJ |
| 作者单位 | Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Geng, SJ,Wang, FH,Zhu, SL. Corrosion behavior of K38G alloy and its nanocrystalline coating in molten sulfate at 900 degrees C[J]. ACTA METALLURGICA SINICA,2002,38(8):871-876. |
| APA | Geng, SJ,Wang, FH,&Zhu, SL.(2002).Corrosion behavior of K38G alloy and its nanocrystalline coating in molten sulfate at 900 degrees C.ACTA METALLURGICA SINICA,38(8),871-876. |
| MLA | Geng, SJ,et al."Corrosion behavior of K38G alloy and its nanocrystalline coating in molten sulfate at 900 degrees C".ACTA METALLURGICA SINICA 38.8(2002):871-876. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。