High temperature corrosion behavior of steel 2.25CrMo in reducing atmosphere containing chlorine
文献类型:期刊论文
作者 | Zhang, K; Niu, Y; Wu, WT |
刊名 | ACTA METALLURGICA SINICA
![]() |
出版日期 | 2003-05-11 |
卷号 | 39期号:5页码:541-543 |
关键词 | steel 2.25CrMo reducing atmosphere containing chlorine high temperature corrosion waste gasification |
ISSN号 | 0412-1961 |
通讯作者 | Zhang, K() |
英文摘要 | The corrosion behavior of steel 2.25CrMo was examined in reducing atmosphere at 500 degreesC and 600 degreesC by TG, SEM/EDX and XRD. The material suffers from accelerated corrosion at both temperatures, and chlorine can be detected at the scale/metal interface. The corrosion kinetics curves transform from parabolic at 500 degreesC to linear at 600 degreesC, which is relevant to vapor pressures of metal chlorides at the corresponding temperatures. The mechanism for the accelerated corrosion by chlorine is discussed. |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
WOS记录号 | WOS:000183358400015 |
出版者 | SCIENCE CHINA PRESS |
源URL | [http://ir.imr.ac.cn/handle/321006/116706] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Zhang, K |
作者单位 | Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, K,Niu, Y,Wu, WT. High temperature corrosion behavior of steel 2.25CrMo in reducing atmosphere containing chlorine[J]. ACTA METALLURGICA SINICA,2003,39(5):541-543. |
APA | Zhang, K,Niu, Y,&Wu, WT.(2003).High temperature corrosion behavior of steel 2.25CrMo in reducing atmosphere containing chlorine.ACTA METALLURGICA SINICA,39(5),541-543. |
MLA | Zhang, K,et al."High temperature corrosion behavior of steel 2.25CrMo in reducing atmosphere containing chlorine".ACTA METALLURGICA SINICA 39.5(2003):541-543. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。