Formation of the high chromium white iron parts with gradient structure via semisolid metal extrusion
文献类型：期刊论文
| 作者 | Yang, Z; Zhang, HF; Wang, AM; Ding, BZ; Hu, ZG |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2003-02-11 |
| 卷号 | 39期号:2页码:164-167 |
| 关键词 | semi-solid metal extrusion high chromium white iron gradient structure |
| ISSN号 | 0412-1961 |
| 通讯作者 | Zhang, HF() |
| 英文摘要 | The high chromium white iron with equiaxed primary structure was extruded at semisolid state. The liquid phase was squeezed out by pressure. After solidification, the volume percentage of the eutectic structure increases gradually from the center to the perimeter. Test shows that the extrusion temperatures have great effect on the structure of the extruded sample. The compact toughness at the center of the sample and the wear resistance at the perimeter of the sample are improved. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000181652500011 |
| 出版者 | SCIENCE CHINA PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/117306]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zhang, HF |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yang, Z,Zhang, HF,Wang, AM,et al. Formation of the high chromium white iron parts with gradient structure via semisolid metal extrusion[J]. ACTA METALLURGICA SINICA,2003,39(2):164-167. |
| APA | Yang, Z,Zhang, HF,Wang, AM,Ding, BZ,&Hu, ZG.(2003).Formation of the high chromium white iron parts with gradient structure via semisolid metal extrusion.ACTA METALLURGICA SINICA,39(2),164-167. |
| MLA | Yang, Z,et al."Formation of the high chromium white iron parts with gradient structure via semisolid metal extrusion".ACTA METALLURGICA SINICA 39.2(2003):164-167. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。