Solidification microstructure and deformation of stainless steel 1Cr18Ni9Ti cast by electromagnetic centrifugal casting
文献类型：期刊论文
| 作者 | Lin, G; Yang, YS; Hua, FA; Guo, DY; Hu, ZQ |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2003-12-01 |
| 卷号 | 39期号:12页码:1233-1237 |
| 关键词 | electromagnetic centrifugal casting stainless steel cold rolling prime dendrite arm space plastic deformation ability |
| ISSN号 | 0412-1961 |
| 通讯作者 | Yang, YS() |
| 英文摘要 | 1Cr18Ni9Ti stainless steel tube blanks were produced by electromagnetic centrifugal casting. It was found that the as-cast microstructure of the blanks was refined due to electromagnetic stirring (EMS). Comparing with the tubes made by ordinary. centrifugal casting, the prime dendrite arm space (40 mum) is decreased by 70%; the yield strength is 274 MPa with a 23% improvement; and the elongation ratio (77%) is improved by 28%. The plastic deformation ability of the tubes was greatly improved by electromagnetic centrifugal casting. Thin-wall tubes of 1Cr18Ni9Ti stainless steel can be cold rolled from the as-cast blanks. The maximum reduction ratio of the tube wall is larger than 91.4% in this experiment. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000187797800001 |
| 出版者 | SCIENCE CHINA PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/117380]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Yang, YS |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Lin, G,Yang, YS,Hua, FA,et al. Solidification microstructure and deformation of stainless steel 1Cr18Ni9Ti cast by electromagnetic centrifugal casting[J]. ACTA METALLURGICA SINICA,2003,39(12):1233-1237. |
| APA | Lin, G,Yang, YS,Hua, FA,Guo, DY,&Hu, ZQ.(2003).Solidification microstructure and deformation of stainless steel 1Cr18Ni9Ti cast by electromagnetic centrifugal casting.ACTA METALLURGICA SINICA,39(12),1233-1237. |
| MLA | Lin, G,et al."Solidification microstructure and deformation of stainless steel 1Cr18Ni9Ti cast by electromagnetic centrifugal casting".ACTA METALLURGICA SINICA 39.12(2003):1233-1237. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。