Low-cycle fatigue of a bulk amorphous alloy Zr41.25Ti13.75Ni10Cu12.5Be22.5
文献类型：期刊论文
| 作者 | Zhang, H; Qiu, KQ; Wang, ZG; Zang, QS; Zhang, HF |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2003-04-11 |
| 卷号 | 39期号:4页码:405-408 |
| 关键词 | Zr base bulk amorphous alloy low-cycle fatigue crystalline phases cyclic strain response |
| ISSN号 | 0412-1961 |
| 通讯作者 | Zhang, H() |
| 英文摘要 | The low-cycle fatigue behavior of Zr41.25Ti13.75Ni10Cu12.5Be22.5 bulk amorphous alloy was investigated in fully reversed stress control at room temperature. Both fully amorphous and partially crystallized specimens show neither cyclic hardening nor softening until final fracture. The fully amorphous alloy has a superior fatigue life than the partially crystallized one. From SEM observations of fracture surfaces and out surfaces of the specimens, the mechanism of stable cyclic strain response is explained. The stages of crack initiation, propagation and overload fracture zone are discernable for the two alloys. The crystalline phases in the amorphous matrix behave more as sites of crack initiation or porosity instead of obstacles retarding crack propagation. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000182921300014 |
| 出版者 | SCIENCE CHINA PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/117611]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zhang, H |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, H,Qiu, KQ,Wang, ZG,et al. Low-cycle fatigue of a bulk amorphous alloy Zr41.25Ti13.75Ni10Cu12.5Be22.5[J]. ACTA METALLURGICA SINICA,2003,39(4):405-408. |
| APA | Zhang, H,Qiu, KQ,Wang, ZG,Zang, QS,&Zhang, HF.(2003).Low-cycle fatigue of a bulk amorphous alloy Zr41.25Ti13.75Ni10Cu12.5Be22.5.ACTA METALLURGICA SINICA,39(4),405-408. |
| MLA | Zhang, H,et al."Low-cycle fatigue of a bulk amorphous alloy Zr41.25Ti13.75Ni10Cu12.5Be22.5".ACTA METALLURGICA SINICA 39.4(2003):405-408. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。