Preparation of Ni-Cr-Co-W-Mo-B brazing filler and its weldability
文献类型：期刊论文
| 作者 | Li, W; Jin, T; Qiao, DC; Sun, XF; Guan, HG; Hu, ZQ |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2003-04-11 |
| 卷号 | 39期号:4页码:444-448 |
| 关键词 | Ni-Cr-Co-W-Mo-B powder wettability the joint microstructure and composition mechamical property |
| ISSN号 | 0412-1961 |
| 通讯作者 | Li, W() |
| 英文摘要 | Ni-Cr-Co-W-Mo-B powder as a brazing filler was prepared by gas atomization, and its microstructure and melting characteristics were determined by XRD and DSC. The microstructure and composition analyses across the bonded interlayer were performed by SEM. The wettability between Ni-Cr-Co-W-Mo-B alloy and Ni-based superalloy substrate is good. The bond tensile strenghth at 1073 K and stress rupture at 1283 K/248 MPa are 1123 MPa and 43 h respectively. After transient liquid phase bonding and heat treatment, the microstructure and composition of the joint zone resemble those of the superalloy substrate, and the joint properties are almost identical to those of the superalloy substrate. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000182921300022 |
| 出版者 | SCIENCE CHINA PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/117753]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Li, W |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Shenyang Inst Technol, Dept Mat Sci & Engn, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Li, W,Jin, T,Qiao, DC,et al. Preparation of Ni-Cr-Co-W-Mo-B brazing filler and its weldability[J]. ACTA METALLURGICA SINICA,2003,39(4):444-448. |
| APA | Li, W,Jin, T,Qiao, DC,Sun, XF,Guan, HG,&Hu, ZQ.(2003).Preparation of Ni-Cr-Co-W-Mo-B brazing filler and its weldability.ACTA METALLURGICA SINICA,39(4),444-448. |
| MLA | Li, W,et al."Preparation of Ni-Cr-Co-W-Mo-B brazing filler and its weldability".ACTA METALLURGICA SINICA 39.4(2003):444-448. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。