Effect of solution temperature on fracture toughness and microstructure of ultra-purified 18Ni(350) maraging steel
文献类型：期刊论文
| 作者 | He, Y; Liu, K; Yang, K |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2003-04-11 |
| 卷号 | 39期号:4页码:381-386 |
| 关键词 | maraging steel solution temperature fracture toughness reverted austenite precipitate segregation ultra-purified melting |
| ISSN号 | 0412-1961 |
| 通讯作者 | He, Y() |
| 英文摘要 | Variation of fracture toughness (K-IC) of an ultra-purified 18Ni (350) maraging steel in the solution temperature range of 1083-1483 K was investigated, and its mechanism was discussed on the base of TEM examination of microstructure in both solution and aging conditions, along with phase transformation and SEM fractographic analysis. The results show that the value of. KIC consistently increases with increasing solution temperature or coarsening of prior austenite grain, and there is no thermal embrittlement resulted from segregation of Ti(C,N) at high solution temperature. Solution treated maraging steel consists of invariable martensite lathes. In aging process, the segregation of precipitates Ni-3 (Mo,Ti) at the prior austenite grain boundaries and lath boundaries becomes more and more serious with the increase of solution temperature or coarsening of prior austenite grain, which leads to the martensite matrix softening and the reverted austenite forms because of enrichment of Ni and Mo at the prior austenite grain boundaries and lath boundaries. The softening matrix and reverted austenite blunt the crack tip and prevent its propagation, so the maraging steel shows a dimpled transgranular fracture and good toughness after high temperature solution treatment. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000182921300010 |
| 出版者 | SCIENCE CHINA PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/117763]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | He, Y |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | He, Y,Liu, K,Yang, K. Effect of solution temperature on fracture toughness and microstructure of ultra-purified 18Ni(350) maraging steel[J]. ACTA METALLURGICA SINICA,2003,39(4):381-386. |
| APA | He, Y,Liu, K,&Yang, K.(2003).Effect of solution temperature on fracture toughness and microstructure of ultra-purified 18Ni(350) maraging steel.ACTA METALLURGICA SINICA,39(4),381-386. |
| MLA | He, Y,et al."Effect of solution temperature on fracture toughness and microstructure of ultra-purified 18Ni(350) maraging steel".ACTA METALLURGICA SINICA 39.4(2003):381-386. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。