The critical temperature for brittle-to-ductile transition of intermetallic compound based on NiAl
文献类型：期刊论文
| 作者 | Ren, WL; Guo, JT; Li, GS; Wu, JS |
| 刊名 | MATERIALS LETTERS
 |
| 出版日期 | 2004-03-01 |
| 卷号 | 58期号:7-8页码:1272-1276 |
| 关键词 | intermetallic compounds mechanical properties NiAl brittle-to-ductile transition tensile critical temperature |
| ISSN号 | 0167-577X |
| DOI | 10.1016/j.matlet.2003.09.020 |
| 通讯作者 | Ren, WL(renweili@eyou.com) |
| 英文摘要 | The brittle-to-ductile transition (BDT) behavior of NiAl-9Mo alloys was firstly investigated to occur in the small temperature range of about 10 degreesC using tensile test method. The characteristic temperature TAB was defined for BDT in the alloy. It associates with the temperature at which the resistance to cleavage starts to sharply increase and the massive dislocation suddenly generates. Therefore, TAB is the critical temperature which symbolizes that the material undergoes the brittle-to-ductile transition. (C) 2003 Elsevier B.V. All rights reserved. |
| WOS研究方向 | Materials Science ; Physics |
| 语种 | 英语 |
| WOS记录号 | WOS:000188763600029 |
| 出版者 | ELSEVIER SCIENCE BV |
| 源URL | [http://ir.imr.ac.cn/handle/321006/119100]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Ren, WL |
| 作者单位 | 1.Shanghai Jiao Tong Univ, Sch Mat Sci & Engn, Minist Educ, Key Lab High Temp Mat, Shanghai 200030, Peoples R China 2.Chinese Acad Sci, Met Res Inst, Dept Superalloys, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Ren, WL,Guo, JT,Li, GS,et al. The critical temperature for brittle-to-ductile transition of intermetallic compound based on NiAl[J]. MATERIALS LETTERS,2004,58(7-8):1272-1276. |
| APA | Ren, WL,Guo, JT,Li, GS,&Wu, JS.(2004).The critical temperature for brittle-to-ductile transition of intermetallic compound based on NiAl.MATERIALS LETTERS,58(7-8),1272-1276. |
| MLA | Ren, WL,et al."The critical temperature for brittle-to-ductile transition of intermetallic compound based on NiAl".MATERIALS LETTERS 58.7-8(2004):1272-1276. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。