Corrosion of pure iron and two commercial steels beneath ZnCl2-Kcl deposits in a controlled atmosphere containing HCl at 500 degrees C
文献类型：期刊论文
| 作者 | Zhang, K; Niu, Y; Wu, WT |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2004-04-01 |
| 卷号 | 40期号:4页码:388-392 |
| 关键词 | pure iron steel NF616 steel SS304 ZnCl2-KCl controlled atmosphere containing HCl corrosion |
| ISSN号 | 0412-1961 |
| 通讯作者 | Zhang, K(kezhang@imr.ac.cn) |
| 英文摘要 | The corrosion behaviours of pure iron and two commercial steels were examined in presence of ZnCl2-KCI deposits in controlled atmosphere containing HCl at 500 degreesC. All of three materials suffered accelerated corrosion by forming thick oxide scales, and complex chlorides mixed molten salts appeared between the oxide scales and substrate materials. However, materials with higher Cr content have better corrosion resistance due to the formation of Fe-Cr spinel or chromia in the inner part of oxide scales. The mechanism for the corrosion accelerated by molten chlorides deposits is discussed. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000221112500012 |
| 出版者 | SCIENCE CHINA PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/119377]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zhang, K |
| 作者单位 | Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, K,Niu, Y,Wu, WT. Corrosion of pure iron and two commercial steels beneath ZnCl2-Kcl deposits in a controlled atmosphere containing HCl at 500 degrees C[J]. ACTA METALLURGICA SINICA,2004,40(4):388-392. |
| APA | Zhang, K,Niu, Y,&Wu, WT.(2004).Corrosion of pure iron and two commercial steels beneath ZnCl2-Kcl deposits in a controlled atmosphere containing HCl at 500 degrees C.ACTA METALLURGICA SINICA,40(4),388-392. |
| MLA | Zhang, K,et al."Corrosion of pure iron and two commercial steels beneath ZnCl2-Kcl deposits in a controlled atmosphere containing HCl at 500 degrees C".ACTA METALLURGICA SINICA 40.4(2004):388-392. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。