Oxidation behaviour of the alloy IC-6 and protective coatings
文献类型：期刊论文
| 作者 | Wang, B; Sun, C; Gong, J; Huang, RF; Wen, LS |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2004-03-01 |
| 卷号 | 46期号:3页码:519-528 |
| 关键词 | superalloy NiCoCrAlY coating oxidation arc ion plating |
| ISSN号 | 0010-938X |
| DOI | 10.1016/S0010-938X(03)00184-7 |
| 通讯作者 | Sun, C(csun@imr.ac.cn) |
| 英文摘要 | In this work, NiCoCrAlY coatings were deposited on a new Ni-base alloy, IC-6. The oxidation kinetic curves of alloy IC-6, K 17 and NiCoCrAlY coatings on alloy IC-6 at 900-1100 degreesC were obtained. The results indicated that the oxide scales consisted of alpha-Al2O3, NiAl2O4, NiO, as well as a small amount of NiMoO4 and MoO2. These scales occurred after alloy IC-6 exposure at 900 degreesC for 100 It. The weight loss occurred when alloy IC-6 were exposed at 1050 and 1100 degreesC due to the formation of volatile MoO3. After the NiCoCrAlY coating was deposited, the scales mainly contained alpha-Al2O3, when the specimens were oxidized at 900 degreesC, and alpha-Al2O3 and Cr2O3 at 1050 degreesC. The formation of alpha-Al2O3 and Cr2O3 scales on NiCoCrAlY coating was directly responsible for improving oxidation resistance of the alloy IC-6. (C) 2003 Elsevier Ltd. All rights reserved. |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000187856800002 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 源URL | [http://ir.imr.ac.cn/handle/321006/119848]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Sun, C |
| 作者单位 | 1.Chinese Acad Sci, Met Res Inst, Dept Surface Engn Mat, Shenyang 110016, Peoples R China 2.Hahn Meitner Inst Berlin GmbH, D-14109 Berlin, Germany |
| 推荐引用方式 GB/T 7714 | Wang, B,Sun, C,Gong, J,et al. Oxidation behaviour of the alloy IC-6 and protective coatings[J]. CORROSION SCIENCE,2004,46(3):519-528. |
| APA | Wang, B,Sun, C,Gong, J,Huang, RF,&Wen, LS.(2004).Oxidation behaviour of the alloy IC-6 and protective coatings.CORROSION SCIENCE,46(3),519-528. |
| MLA | Wang, B,et al."Oxidation behaviour of the alloy IC-6 and protective coatings".CORROSION SCIENCE 46.3(2004):519-528. |