Recrystallization and fatigue failure of DS alloy blades
文献类型：期刊论文
| 作者 | Zhang, WF; Li, YJ; Liu, GY; Zhao, AG; Tao, CH; Tian, JF; Yao, G |
| 刊名 | ENGINEERING FAILURE ANALYSIS
 |
| 出版日期 | 2004-06-01 |
| 卷号 | 11期号:3页码:429-437 |
| ISSN号 | 1350-6307 |
| 关键词 | recrystallization directionally solidified alloys blade failures fatigue failure heat treatment |
| DOI | 10.1016/j.engfailanal.2003.05.014 |
| 通讯作者 | Zhang, WF(weifangzhang831@sohu.com) |
| 英文摘要 | This paper analyzed cracks and fractures of DS alloy blades. The failure modes and causes were studied on the basis of fracture surfaces and metallographical examination, and prevention measures were given. The results showed that the cracks and fractures failed in the same mode-fatigue failure caused by surface recrystallization of the blades. The surface recrystallization formed during the solution heat treatment because the blades deformed plastically. (C) 2003 Elsevier Ltd. All rights reserved. |
| WOS研究方向 | Engineering ; Materials Science |
| 语种 | 英语 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| WOS记录号 | WOS:000220514000014 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/120009]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Zhang, WF |
| 作者单位 | 1.Inst Aeronaut Mat, Failure Anal Ctr, AVIC, Beijing 100095, Peoples R China 2.Chinese Acad Sci, Met Res Inst, Shenyang 110035, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, WF,Li, YJ,Liu, GY,et al. Recrystallization and fatigue failure of DS alloy blades[J]. ENGINEERING FAILURE ANALYSIS,2004,11(3):429-437. |
| APA | Zhang, WF.,Li, YJ.,Liu, GY.,Zhao, AG.,Tao, CH.,...&Yao, G.(2004).Recrystallization and fatigue failure of DS alloy blades.ENGINEERING FAILURE ANALYSIS,11(3),429-437. |
| MLA | Zhang, WF,et al."Recrystallization and fatigue failure of DS alloy blades".ENGINEERING FAILURE ANALYSIS 11.3(2004):429-437. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。