EFFECT OF LONG-TERM AGING AT 760 degrees C ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF A Ni-Cr-W-Fe ALLOY
文献类型：期刊论文
| 作者 | Hao Xianchao; Zhang Long; Xiong Chao; Ma Yingche; Liu Kui |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2015-07-11 |
| 卷号 | 51期号:7页码:807-814 |
| 关键词 | Ni-Cr-W-Fe alloy long-term aging gamma'phase tensile property |
| ISSN号 | 0412-1961 |
| 通讯作者 | Ma Yingche(ycma@imr.ac.cn) |
| 英文摘要 | Significant efforts on development of advanced ultra-supercritical (A-USC) fossil fired power plants with steam conditions of 700 degrees C and 30 MPa or higher have been made in recent years. The most important consideration is the development of materials for superheater and reheater tubes with working temperature as high as 760 degrees C. During the design and application of these materials, phase stability, creep rupture strength and corrosion performance at 700 similar to 760 degrees C should be evaluated. A new type Ni-Cr-W-Fe alloy has been designed for A-USC power plants and the microstructure and mechanical properties of Ni-Cr-W-Fe alloy after long-term aging at 760 degrees C was investigated using OM, SEM, TEM and tensile testing in this work. The fractographs of tensile samples were observed. The results show that the average gain size of specimen after solution-annealing at 1100 degrees C is about 80 mu m with twin planes present in the matrix. The major precipitates after aging at 760 degrees C for 16 h are M23C6 and gamma'. The average particle size and the volume fraction of gamma'phase are approximately 29 nm and 19%, respectively. The coarsening behavior of gamma' during long-term aging at 760 degrees C follows Ostwald ripening theory. The solution-annealed Ni-Cr-W-Fe alloy performs excellent ductility at room temperature and the fracture mode of is ductile. The room temperature tensile strengths increase obviously with the decreasing of elongation and reduction of area after aging treatment. The yield strengths at both room and elevated temperatures decrease gradually with the extending aging time at 760 degrees C. The tensile ductility at room temperature of Ni-Cr-W-Fe alloy decreases after aging from 1000 to 3000 h, while the elevated temperature ductility varies mildly and keeps at approximately 15%. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000358471900006 |
| 出版者 | SCIENCE PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/120459]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Ma Yingche |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Hao Xianchao,Zhang Long,Xiong Chao,et al. EFFECT OF LONG-TERM AGING AT 760 degrees C ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF A Ni-Cr-W-Fe ALLOY[J]. ACTA METALLURGICA SINICA,2015,51(7):807-814. |
| APA | Hao Xianchao,Zhang Long,Xiong Chao,Ma Yingche,&Liu Kui.(2015).EFFECT OF LONG-TERM AGING AT 760 degrees C ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF A Ni-Cr-W-Fe ALLOY.ACTA METALLURGICA SINICA,51(7),807-814. |
| MLA | Hao Xianchao,et al."EFFECT OF LONG-TERM AGING AT 760 degrees C ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF A Ni-Cr-W-Fe ALLOY".ACTA METALLURGICA SINICA 51.7(2015):807-814. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。