CORROSION BEHAVIOR OF GH3535 SUPERALLOY IN FLiNaK MOLTEN SALT
文献类型：期刊论文
| 作者 | Liu Tao3,4; Dong Jiasheng4; Xie Guang4; Wang Yisheng1; Li Hui4; Li Zhijun2; Zhou Xingtai2; Lou Langhong4 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2015-09-11 |
| 卷号 | 51期号:9页码:1059-1066 |
| 关键词 | GH3535 alloy FLiNaK molten salt Al2O3 coating corrosion |
| ISSN号 | 0412-1961 |
| 通讯作者 | Dong Jiasheng(djs@imrac.cn) |
| 英文摘要 | As one of the most promising next generation reactors, the molten salt breeder reactor (MSBR) with excellent inherence security has attracted more and more attentions in recent years due to energy shortage and the security problem of traditional nuclear reactor. The most significant service characteristic of the structural material used in MSBR is the existence of FLiNaK molten salt compared with other nuclear reactors. FLiNaK molten salt is very corrosive to the structural material in the reactor, and affects the safety operation of nuclear power plants. A polycrystalline Ni-Mo-Cr-Fe superalloy was developed and used as an important structural material in MSBR at Oak Ridge National Laboratory (ORNL), but the corrosion mechanism of the alloy in FLiNaK molten salt has not been determined since the study terminated in 1970's as some politic reasons. Alloy served in harsh environments, often using protective coating to improve the corrosion properties. While few works about the coating. corrosion resistance in FLiNaK molten salt were reported at present. Al2O3 and Cr2O3 coatings usually have excellent corrosion resistance in molten salt, such as sulphate, nitrate and halide molten salt. But, whether the oxide film has corrosion resistance in FLiNaK molten salt has not been determined. In this work, the corrosion mechanism of alloy in FLiNaK molten salt was studied by using immersion corrosion experiment through the method of SEM, EDS and XRD. The influence of Al2O3 coating on corrosion resistance in FLiNaK molten salt was also investigated. The results show that the Al2O3 coating does not affect the exsolution corrosion characteristics of Cr and Mo elements in FLiNaK molten salt at 700 degrees C for 400 h. The different is that naked alloy exhibits intergranular corrosion characteristic, and the alloy with Al2O3 coating exhibits spot corrosion characteristic. The Al2O3 coating cannot improve the corrosion resistance of the alloy in FLiNaK molten salt. The Al2O3 film dissolved in molten salt and resulted in the exposure of the alloy surface. The corrosion rate was increased since the formation of corrosion cell between oxide film and the exposed alloy surface. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000362617700004 |
| 出版者 | SCIENCE PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/120956]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Dong Jiasheng |
| 作者单位 | 1.AVIC China Natl South Aviat Ind Co Ltd, Power Branch, Zhuzhou 412002, Peoples R China 2.Chinese Acad Sci, Shanghai Inst Appl Phys, Shanghai 201800, Peoples R China 3.Dalian Univ Technol, Sch Mat Sci & Engn, Dalian 116024, Peoples R China 4.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liu Tao,Dong Jiasheng,Xie Guang,et al. CORROSION BEHAVIOR OF GH3535 SUPERALLOY IN FLiNaK MOLTEN SALT[J]. ACTA METALLURGICA SINICA,2015,51(9):1059-1066. |
| APA | Liu Tao.,Dong Jiasheng.,Xie Guang.,Wang Yisheng.,Li Hui.,...&Lou Langhong.(2015).CORROSION BEHAVIOR OF GH3535 SUPERALLOY IN FLiNaK MOLTEN SALT.ACTA METALLURGICA SINICA,51(9),1059-1066. |
| MLA | Liu Tao,et al."CORROSION BEHAVIOR OF GH3535 SUPERALLOY IN FLiNaK MOLTEN SALT".ACTA METALLURGICA SINICA 51.9(2015):1059-1066. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。