Crystallization Behavior of Glass Ceramic Filler During Joining Process
文献类型:期刊论文
作者 | Zhu Wei-Wei2; Chen Ji-Chun1 |
刊名 | JOURNAL OF INORGANIC MATERIALS |
出版日期 | 2015-12-01 |
卷号 | 30期号:12页码:1310-1314 |
ISSN号 | 1000-324X |
关键词 | alumina glass ceramic joining crystallization behavior |
通讯作者 | Zhu Wei-Wei(wwzhu@ccut.edu.cn) |
英文摘要 | A CaO-Al2O3-SiO2 system glass ceramic with addition of Li2O and Fe2O3 was developed to join alumina ceramics. The crystallization behavior of the glass interlayer during joining process was investigated by DTA, SEM and XRD. The effect of joint microstructure and phase composition on the joint strength was study. The results show that LiAlSi2O6, CaSiO3, Ca3Fe2Si3O12, and CaAl2Si2O8 are formed in the glass during conventional crystallization treatment. However, when the glass was used to join alumina, the crystallization behavior of the glass interlayer is closely related to the heating cycle. Direct cooling from joining temperature leads to completely amorphous interlayer formation, due to the absence of enough nucleation driving force. An extra nucleation-crystallization treatment during cooling contributes to crystallization of the glass interlayer in joints. Meannhile, the phase composition of glass interlayer can be adjusted by changing the crystallization temperature according to the DTA results. In addition, the joint strength is highly sensitive to crystalline phases in the interlayer. When there is only CaAl2Si2O8 formed in the interlayer, the joint strength reaches as high as 247.5 MPa. By contrast, when there is LiAlSi2O6 or Ca3Fe2Si3O12 formed in the interlayer, the joint strength is only 10-135 MPa. |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | SCIENCE PRESS |
WOS记录号 | WOS:000367759000012 |
源URL | [http://ir.imr.ac.cn/handle/321006/121448] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Zhu Wei-Wei |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Changchun Univ Technol, Sch Mat Sci & Engn, Changchun 130012, Peoples R China |
推荐引用方式 GB/T 7714 | Zhu Wei-Wei,Chen Ji-Chun. Crystallization Behavior of Glass Ceramic Filler During Joining Process[J]. JOURNAL OF INORGANIC MATERIALS,2015,30(12):1310-1314. |
APA | Zhu Wei-Wei,&Chen Ji-Chun.(2015).Crystallization Behavior of Glass Ceramic Filler During Joining Process.JOURNAL OF INORGANIC MATERIALS,30(12),1310-1314. |
MLA | Zhu Wei-Wei,et al."Crystallization Behavior of Glass Ceramic Filler During Joining Process".JOURNAL OF INORGANIC MATERIALS 30.12(2015):1310-1314. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。