EFFECTS OF HIGH TEMPERATURE SHORT TIME AGEING TREATMENT ON THE MICROSTRUCTURES AND MECHANICAL PROPERTIES OF Mg-3Nd-1Zn ALLOY
文献类型：期刊论文
| 作者 | Wang Wenhui1,2; Wu Di1; Chen Rongshi1; Lou Changsheng2 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2016-05-11 |
| 卷号 | 52期号:5页码:567-574 |
| 关键词 | magnesium alloy ageing treatment precipitate mechanical property |
| ISSN号 | 0412-1961 |
| DOI | 10.11900/0412.1961.2015.00333 |
| 通讯作者 | Wu Di(dwu@imr.ac.cn) |
| 英文摘要 | Among the traditional cast magnesium alloys system, Mg-3Nd-1Zn alloy with high strength and heat resistance, has been widely applied in aeronautics such as in engine box and wing rib of airplane. In present research, the as-cast Mg-2.7Nd-0.6Zn-0.5Zr (NZ31) alloy was solution treated and then aged at temperatures ranging from 200 degrees C to 300 degrees C. The microstructures and mechanical properties of the aged specimens especially at relatively high temperature (225 similar to 300 degrees C) were systematically characterized by OM, SEM and TEM. A new kind of precipitates distributed in line was clearly found in the specimens aged at high temperature (225 similar to 275 degrees C) for a short time (15 similar to 30 min), which corresponded to a significant enhancement of hardness and tensile strength at room temperature. The TEM results showed that the precipitates distributed in line had a composition of Mg12Nd and a granular shape, and mainly formed along the (0001)(Mg) basal plane. The special distribution of the granular Mg12Nd precipitates was effective barriers to the basal slips and may probably restrain the intergranular coordination during tensile deformation, leading to a large strengthening effect, that is, the yield strength and ultimate tensile strength, of the NZ31 alloy aged at 250 similar to 275 degrees C for 20 similar to 30 min, increased by about 70% and 29% respectively, in comparison with only the solutionized one. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000376471100007 |
| 出版者 | SCIENCE PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/122250]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wu Di |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Shenyang Ligong Univ, Sch Mat Sci & Engn, Shenyang 110159, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang Wenhui,Wu Di,Chen Rongshi,et al. EFFECTS OF HIGH TEMPERATURE SHORT TIME AGEING TREATMENT ON THE MICROSTRUCTURES AND MECHANICAL PROPERTIES OF Mg-3Nd-1Zn ALLOY[J]. ACTA METALLURGICA SINICA,2016,52(5):567-574. |
| APA | Wang Wenhui,Wu Di,Chen Rongshi,&Lou Changsheng.(2016).EFFECTS OF HIGH TEMPERATURE SHORT TIME AGEING TREATMENT ON THE MICROSTRUCTURES AND MECHANICAL PROPERTIES OF Mg-3Nd-1Zn ALLOY.ACTA METALLURGICA SINICA,52(5),567-574. |
| MLA | Wang Wenhui,et al."EFFECTS OF HIGH TEMPERATURE SHORT TIME AGEING TREATMENT ON THE MICROSTRUCTURES AND MECHANICAL PROPERTIES OF Mg-3Nd-1Zn ALLOY".ACTA METALLURGICA SINICA 52.5(2016):567-574. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。