INFLUENCE OF Re ON MICROSTRUCTURES OF A DIRECTIONALLY SOLIDIFIED Ni-BASED SUPERALLOY
文献类型：期刊论文
| 作者 | Zhang Siqian2; Wang Dong1; Wang Di1; Peng Jianqiang3 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2016-07-01 |
| 卷号 | 52期号:7页码:851-858 |
| 关键词 | Ni-based superalloy directional solidification Re mu phase grain boundary carbide |
| ISSN号 | 0412-1961 |
| DOI | 10.11900/0412.1961.2015.00600 |
| 通讯作者 | Wang Dong(dwang@imr.ac.cn) |
| 英文摘要 | Up to now, considerable effort has been expended in attempts to investigate the influences of Re on Ni-based single crystal superalloys. However, few study had elucidated the influences of Re on carbide, boride and grain boundary. Therefore, the influence of a 2% Re (mass fraction) addition on the as-cast and heat-treated microstructures of a Ni-based directionally solidified superalloy was investigated by comparison with Re-free alloy using SEM, EPMA and TEM. The results show that Re accelerates the precipitation of mu phase in the periphery of eutectic and at grain boundary for as-cast microstructure. After heat treatment, Re also accelerates the precipitation of phase in the vicinity of primary MC carbide and at grain boundary. For 0Re alloy, there are small number of M6C carbide in the vicinity of primary MC carbide and M-23(C, B)(6) boro-carbide at grain boundary. For 2Re alloy, a large amount of blocky mu phase enveloped by thick gamma'-film is found in the vicinity of primary MC carbide and at grain boundary. Enrichment of B along the grain boundary is observed in 0Re alloy. On the contrary, relatively uniform distribution of B is found in 2Re alloy. The precipitation mechanism of mu phase during the process of heat treatment is also analyzed. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000385747800010 |
| 出版者 | SCIENCE PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/122988]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wang Dong |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Shenyang Univ Technol, Sch Mat Sci & Engn, Shenyang 110870, Peoples R China 3.Harbin Turbine Co Ltd, Harbin 150046, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang Siqian,Wang Dong,Wang Di,et al. INFLUENCE OF Re ON MICROSTRUCTURES OF A DIRECTIONALLY SOLIDIFIED Ni-BASED SUPERALLOY[J]. ACTA METALLURGICA SINICA,2016,52(7):851-858. |
| APA | Zhang Siqian,Wang Dong,Wang Di,&Peng Jianqiang.(2016).INFLUENCE OF Re ON MICROSTRUCTURES OF A DIRECTIONALLY SOLIDIFIED Ni-BASED SUPERALLOY.ACTA METALLURGICA SINICA,52(7),851-858. |
| MLA | Zhang Siqian,et al."INFLUENCE OF Re ON MICROSTRUCTURES OF A DIRECTIONALLY SOLIDIFIED Ni-BASED SUPERALLOY".ACTA METALLURGICA SINICA 52.7(2016):851-858. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。