EFFECT OF HOT ISOSTATIC PRESSING PARAMETERS ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF POWDER METALLURGY Ti-5Al-2.5Sn ELI ALLOY
文献类型：期刊论文
| 作者 | Guo Ruipeng1,3; Xu Lei3; Cheng Wenxiang2; Lei Jiafeng3; Yang Rui3 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2016-07-01 |
| 卷号 | 52期号:7页码:842-850 |
| 关键词 | Ti-5Al-2.5Sn ELI powder metallurgy hot isostatic pressing shielding effect |
| ISSN号 | 0412-1961 |
| DOI | 10.11900/0412.1961.2016.00018 |
| 通讯作者 | Xu Lei(lxu@imr.ac.cn) |
| 英文摘要 | Near-net-shape forming through powder metallurgy (PM) route is a cost-efficient approach to produce the hard-to-machining materials such as titanium alloys. Hot isostatic pressing (HIPing) is a common technique to fabricate PM titanium alloys and components. Prealloyed powder metallurgy through HIPing is considered as upgrade of precision casting for titanium alloys. Ti-5Al-2.5Sn ELI (extra-low interstitial) is a typical alpha-Ti alloy, which is widely used at cryogenic temperature. In this work, the Ti-5Al-2.5Sn ELI prealloyed powder was produced by electrode induction melting gas atomization. Characterization of the prealloyed powder was carried out to understand the following HIPing process. The influence of HIPing parameters on microstructure and mechanical properties of Ti-5Al-2.5Sn ELI powder compact was studied. The results show that the relative density of powder compact increases with the increasing of HIPing temperature and pressure. The mechanical properties of powder compact can achieve those of wrought materials, when the relative density is more than 99.5%. To balance the relative density, microstructure and mechanical properties of the powder compacts, the optimized HIPing parameters for Ti-5Al-2.5Sn ELI powder are temperature in the range of 890 similar to 940 degrees C, pressure above 120 MPa and holding for 3 h. The shielding effect of capsule will hinder the powder densification during HIPing process, which will likely cause non-uniform densification and degrade the relative density of powder compact. However, the shield effect can be weakened through proper tooling design and optimization of the HIPing procedure. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000385747800009 |
| 出版者 | SCIENCE PRESS |
| 源URL | [http://ir.imr.ac.cn/handle/321006/123034]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Xu Lei |
| 作者单位 | 1.Northeastern Univ, Sch Mat Sci & Engn, Shenyang 110819, Peoples R China 2.Res Inst Baoshan Iron & Steel Co Ltd, Shanghai 201900, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Guo Ruipeng,Xu Lei,Cheng Wenxiang,et al. EFFECT OF HOT ISOSTATIC PRESSING PARAMETERS ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF POWDER METALLURGY Ti-5Al-2.5Sn ELI ALLOY[J]. ACTA METALLURGICA SINICA,2016,52(7):842-850. |
| APA | Guo Ruipeng,Xu Lei,Cheng Wenxiang,Lei Jiafeng,&Yang Rui.(2016).EFFECT OF HOT ISOSTATIC PRESSING PARAMETERS ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF POWDER METALLURGY Ti-5Al-2.5Sn ELI ALLOY.ACTA METALLURGICA SINICA,52(7),842-850. |
| MLA | Guo Ruipeng,et al."EFFECT OF HOT ISOSTATIC PRESSING PARAMETERS ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF POWDER METALLURGY Ti-5Al-2.5Sn ELI ALLOY".ACTA METALLURGICA SINICA 52.7(2016):842-850. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。