Effects of Re-Melting Processes on the Tensile Properties of K452 Alloy at High Temperature
文献类型：期刊论文
| 作者 | Yang Jinxia2; Xu Futao2; Zhou Donglin1; Sun Yuan2; Hou Xingyu2; Cui Chuanyong2 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2017-06-01 |
| 卷号 | 53期号:6页码:703-708 |
| 关键词 | superalloy tensile property shrinkage |
| ISSN号 | 0412-1961 |
| DOI | 10.11900/0412.1961.2016.00286 |
| 通讯作者 | Yang Jinxia(jxyang@imr.ac.cn) |
| 英文摘要 | K452 alloy is a nickel-based cast superalloy having the good tensile properties at high temperature and excellent corrosion resistance. It has been applied as a blade material of engines when environmental temperature is not above 950 degrees C. It is found that the tensile properties of the alloy have become more scattered and unstable although its chemical compositions are not changed. Hence, the tensile properties of the alloy were studied in order to increase its stability at high temperature and improve its applied properties. Tensile specimens were prepared using the different re-melting processes. Tensile tests were done at 900 degrees C. When the pouring temperature was 1430 degrees C, tensile properties were not only lower than expected, but also had great degree of dispersion, i.e., the vales of ultimate strengths changed in the range of 410 MPa and 510 MPa, and the elongations changed in the range of 3.5% and 22.0%, the average contents of O and N were the highest among three tested conditions. The highest N content was 0.0028%. And the shrinkage area was higher than those in other two re-melting processes. When the pouring temperature was 1500 degrees C, the tensile properties were improved, and their changing scopes became small, the average contents of O and N decreased, the shrinkage area decreased. When the refining temperature was 1590 degrees C and the holding time was 5 min, both average contents of O and N were decreased greatly, the shrinkage was not seen in the fracture surfaces. And the tensile properties were improved. Furthermore, their changing scopes were very small. |
| 资助项目 | National Natural Science Foundation of China[11332010] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000405561500008 |
| 出版者 | SCIENCE PRESS |
| 资助机构 | National Natural Science Foundation of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/124704]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Yang Jinxia |
| 作者单位 | 1.Harbin Dongan Engine Grp Corp LTD, Harbin 150066, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yang Jinxia,Xu Futao,Zhou Donglin,et al. Effects of Re-Melting Processes on the Tensile Properties of K452 Alloy at High Temperature[J]. ACTA METALLURGICA SINICA,2017,53(6):703-708. |
| APA | Yang Jinxia,Xu Futao,Zhou Donglin,Sun Yuan,Hou Xingyu,&Cui Chuanyong.(2017).Effects of Re-Melting Processes on the Tensile Properties of K452 Alloy at High Temperature.ACTA METALLURGICA SINICA,53(6),703-708. |
| MLA | Yang Jinxia,et al."Effects of Re-Melting Processes on the Tensile Properties of K452 Alloy at High Temperature".ACTA METALLURGICA SINICA 53.6(2017):703-708. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。