Effects of Annealing Process on Microstructure and Mechanical Properties of TC6 Titanium Alloy Bars
文献类型：期刊论文
| 作者 | Lei Xiaofei; Dong Limin; Zhang Zhiqiang; Ba Hongbo; Wang Haizhong; Yang Rui |
| 刊名 | RARE METAL MATERIALS AND ENGINEERING
 |
| 出版日期 | 2017-06-01 |
| 卷号 | 46页码:80-84 |
| 关键词 | TC6 titanium alloy annealing temperature cooling mode microstructure mechanical properties |
| ISSN号 | 1002-185X |
| 通讯作者 | Dong Limin(lmdong@imr.ac.cn) |
| 英文摘要 | Effects of annealing temperature, cooling mode and isothermal annealing process on microstructure and mechanical properties of TC6 titanium alloy bars were studied. The results show that when specimens are annealed at 800 similar to 840 degrees C with air cooling, equiaxed microstructure forms and strength decreases slightly with increasing the annealing temperature. Bimodal microstructure forms due to secondary alpha phase precipitate in beta matrix after annealing at 880 degrees C with air cooling, which lead to the maximum strength and little decrease in plasticity. With further increasing of annealing temperature, microstructure is coarsend obviously, so strength and plasticity decrease. Fine acicular Widmanstatten structure is obtained above the beta transus, which lead to increase in strength but significantly decrease in plasticity. When specimens are annealed at 800 similar to 1000 degrees C with furnace cooling, there are two obvious differences of microstructure evolution between air-cooled and furnace-cooled specimens. Firstly, compared with air-cooled specimens, the annealing temperature of forming bimodal microstructure is higher and secondary alpha phase does not obviously precipitate in beta matrix below the beta transus. Secondly, lamellar Widmanstatten is obtained above the beta transus. The strength of furnace-cooled specimens decreases with increasing the temperature, and the change of plasticity is not significant. In addition, the maximum value of impact toughness occurs after annealing at 880 degrees C with furnace cooling. The excellent matching of strength, plasticity and impact toughness is obtained after isothermal annealing (880 degrees C, 2 h, FC to 650 degrees C, 2 h, AC), which is similiar to that of furnace-cooled specimen annealed at 880 degrees C. |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000406570100017 |
| 出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
| 源URL | [http://ir.imr.ac.cn/handle/321006/124855]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Dong Limin |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Lei Xiaofei,Dong Limin,Zhang Zhiqiang,et al. Effects of Annealing Process on Microstructure and Mechanical Properties of TC6 Titanium Alloy Bars[J]. RARE METAL MATERIALS AND ENGINEERING,2017,46:80-84. |
| APA | Lei Xiaofei,Dong Limin,Zhang Zhiqiang,Ba Hongbo,Wang Haizhong,&Yang Rui.(2017).Effects of Annealing Process on Microstructure and Mechanical Properties of TC6 Titanium Alloy Bars.RARE METAL MATERIALS AND ENGINEERING,46,80-84. |
| MLA | Lei Xiaofei,et al."Effects of Annealing Process on Microstructure and Mechanical Properties of TC6 Titanium Alloy Bars".RARE METAL MATERIALS AND ENGINEERING 46(2017):80-84. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。