OXIDATION RESISTANCE OF TIAL IMPROVED BY COCRAL AND COCRALY COATING
文献类型：期刊论文
| 作者 | TANIGUCHI, S; ASANUMA, N; SHIBATA, T; WANG, FH; LOU, HY; WU, WT |
| 刊名 | JOURNAL OF THE JAPAN INSTITUTE OF METALS
 |
| 出版日期 | 1993-07-01 |
| 卷号 | 57期号:7页码:781-789 |
| ISSN号 | 0021-4876 |
| 关键词 | COCRAL COCRALY COATING TIAL HIGH TEMPERATURE OXIDATION RESISTANCE AL2O3 SCALE |
| 通讯作者 | TANIGUCHI, S() |
| 英文摘要 | Oxidation resistance of TiAl coupons coated with Co-30Cr-4Al and Co-30Cr-4Al-0.2Y (mass%) coatings has been assessed by isothermal oxidation test in a temperature range 1100 to 1400 K and by cyclic oxidation test at 1200 K. The coating, consisting of very fine grains, was prepared by magnetron sputtering with resulting thicknesses of 30-40 mum. Both the coatings are very effective to suppress the oxidation below 1300 K. This effect is attributable to the formation of alpha-alumina scales. However, after long oxidation periods, the oxidation manner changes from parabolic to accelerated oxidation. This acceleration is explained in terms of local growth of rutile on the scale. Relatively large voids are formed at the scale/coating interface, within the coating, and the coating/substrate interface. The addition of Y to the coating results in the flat scales with no voids at the scale/coating interface, though the oxidation rate slightly increases and the recrystallization of the coating is delayed. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | JAPAN INST METALS |
| WOS记录号 | WOS:A1993LP50900009 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/126549]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | TANIGUCHI, S |
| 作者单位 | CHINESE ACAD SCI, INST CORROS & PROTECT MET, CORROS SCI LAB, SHENYANG, PEOPLES R CHINA |
| 推荐引用方式 GB/T 7714 | TANIGUCHI, S,ASANUMA, N,SHIBATA, T,et al. OXIDATION RESISTANCE OF TIAL IMPROVED BY COCRAL AND COCRALY COATING[J]. JOURNAL OF THE JAPAN INSTITUTE OF METALS,1993,57(7):781-789. |
| APA | TANIGUCHI, S,ASANUMA, N,SHIBATA, T,WANG, FH,LOU, HY,&WU, WT.(1993).OXIDATION RESISTANCE OF TIAL IMPROVED BY COCRAL AND COCRALY COATING.JOURNAL OF THE JAPAN INSTITUTE OF METALS,57(7),781-789. |
| MLA | TANIGUCHI, S,et al."OXIDATION RESISTANCE OF TIAL IMPROVED BY COCRAL AND COCRALY COATING".JOURNAL OF THE JAPAN INSTITUTE OF METALS 57.7(1993):781-789. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。