Study on the Galvanic Current of Corrosion Behavior for AH32 Long-Scale Specimen in Simulated Tidal Zone
文献类型：期刊论文
| 作者 | Zhao Lin; Mu Xin; Dong Junhua; Wu Liping; Wang Changgang; Ke Wei |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2017-11-11 |
| 卷号 | 53期号:11页码:1445-1452 |
| ISSN号 | 0412-1961 |
| 关键词 | AH32 steel tidal zone long-scale specimen galvanic current potential |
| DOI | 10.11900/0412.1961.2017.00076 |
| 通讯作者 | Dong Junhua(jhdong@imr.ac.cn) |
| 英文摘要 | The environment of the tidal zone is very complex. The interactions of dry-wet alternation and sea erosion lead to serious corrosion of steel structures, which makes it difficult to adopt protective methods. Therefore, it is of great significance to study the corrosion and protection methods of steel in tidal zone. For long-scale steel through the tidal zone and immersion zone, there is a big difference in corrosion behavior with complete immersion condition, the potential of the steel surface changes due to the influence of oxygen concentration difference and tidal fluctuations or other factors. In this study, the galvanic current and open circuit potential of the long-scale AH32 steel were monitored in simulated tidal zone. The results shows that the potential at different tide levels and different immersion depths for a long-scale AH32 specimen is not unified, with the macro cell was formed by the difference of oxygen supply, which caused internal galvanic current. The essence of the galvanic current is the net current that was generated by the sum of anode and cathode current. Galvanic current at different positions on the long-scale AH32 specimen varies with the tidal movement periodically in tidal zone. When tide is at the highest level, the galvanic current of all parts accesses a maximum value, and among these maximum values, the largest one is at the middle part of specimen, which causes the biggest anodic dissolution current density. According to the variation of the galvanic current, the time distributions of the drying, wetting and immersion states were calculated, and the results showed that the corrosion scale of the long-scale AH32 specimen at different positions depends on the time all location of wetting and immersion in tidal zone. The macro cell caused the galvanic current when all parts of the specimen were immersed. At wetting state, the solution resistance of the thin liquid film is very large, which leads to the change of the driving potential of the macro cell into the potential drop. Thus, macro cell is ineffective in the wetting state and cannot produce the galvanic current. According to the relation between wetting time and quantity of electricity at wetting state, the maximum wetting time of the long-scale AH32 specimen is shown above average mean tide level in tidal zone, which indicates that the corrosion loss of this part is maximum due to wetting state. In addition to weight loss measurements, maximum of it for long-scale AH32 specimen was obtained at the average mean tide level caused by immersion state. It can be indicated the maximum weight loss of the long-scale AH32 specimen should appear upper the average mean tide level part in tidal zone. These results were consistent with measurements of corrosion rates. |
| 资助项目 | National Natural Science Foundation of China[51671200] ; High Technology Research and Development Program of China[2015AA034301] ; National Corrosion Platform Fund ; Key Laboratory of Marine Environment Corrosion and Biofouling Fund[MCKF201611] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | SCIENCE PRESS |
| WOS记录号 | WOS:000416301500004 |
| 资助机构 | National Natural Science Foundation of China ; High Technology Research and Development Program of China ; National Corrosion Platform Fund ; Key Laboratory of Marine Environment Corrosion and Biofouling Fund |
| 源URL | [http://ir.imr.ac.cn/handle/321006/127104]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Dong Junhua |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhao Lin,Mu Xin,Dong Junhua,et al. Study on the Galvanic Current of Corrosion Behavior for AH32 Long-Scale Specimen in Simulated Tidal Zone[J]. ACTA METALLURGICA SINICA,2017,53(11):1445-1452. |
| APA | Zhao Lin,Mu Xin,Dong Junhua,Wu Liping,Wang Changgang,&Ke Wei.(2017).Study on the Galvanic Current of Corrosion Behavior for AH32 Long-Scale Specimen in Simulated Tidal Zone.ACTA METALLURGICA SINICA,53(11),1445-1452. |
| MLA | Zhao Lin,et al."Study on the Galvanic Current of Corrosion Behavior for AH32 Long-Scale Specimen in Simulated Tidal Zone".ACTA METALLURGICA SINICA 53.11(2017):1445-1452. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。