Microstructures of Nickel-base Single-Crystal Superalloy Prepared by Laser Solid Forming
文献类型：期刊论文
| 作者 | Liang Jingjing; Yang Yanhong; Zhou Yizhou; Li Jinguo; Wang Liang; Jin Tao; Sun Xiaofeng |
| 刊名 | RARE METAL MATERIALS AND ENGINEERING
 |
| 出版日期 | 2017-12-01 |
| 卷号 | 46期号:12页码:3753-3759 |
| 关键词 | laser solid forming single crystal superalloy heat treatment recrystallization |
| ISSN号 | 1002-185X |
| 通讯作者 | Liang Jingjing(jjliang@imr.ac.cn) |
| 英文摘要 | Single-crystal superalloys have been commonly used in modern advanced aero engines to produce high-pressure high-temperature turbine blades. In order to extend the lifetime of single-crystal turbine blades, repair of cracked and worn ones is of great interest. Laser Solid Forming (LSF) is a prospective technology that can be used to repair single-crystal blades. In this study, the microstructure of the as-deposited and heat-treated LSF single-crystal superalloy has been characterized through optical microscopy (OM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The as-deposited LSF sample shows a directionally solidified columnar dendrites growing almost parallel to the building direction. Between the dendrites, nearly round microporosity and blocky MC carbide particles are dispersed uniformly. TEM results indicate that many nano gamma' particles precipitate in gamma matrix. In addition, during LSF deposition process, stress is formed, which generates plenty of dislocations. During heat treatment, the LSF sample experiences full recrystallization. The recrystallization grains are in different sizes, and twins are found in some recrystallized grains. Because the residual stress is fully released during heat treatment, the size and shape of gamma' precipitates in the recrystallized and un-recrystallized regions are similar to those in conventionally cast samples. |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000425203200028 |
| 出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
| 源URL | [http://ir.imr.ac.cn/handle/321006/127395]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Liang Jingjing |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liang Jingjing,Yang Yanhong,Zhou Yizhou,et al. Microstructures of Nickel-base Single-Crystal Superalloy Prepared by Laser Solid Forming[J]. RARE METAL MATERIALS AND ENGINEERING,2017,46(12):3753-3759. |
| APA | Liang Jingjing.,Yang Yanhong.,Zhou Yizhou.,Li Jinguo.,Wang Liang.,...&Sun Xiaofeng.(2017).Microstructures of Nickel-base Single-Crystal Superalloy Prepared by Laser Solid Forming.RARE METAL MATERIALS AND ENGINEERING,46(12),3753-3759. |
| MLA | Liang Jingjing,et al."Microstructures of Nickel-base Single-Crystal Superalloy Prepared by Laser Solid Forming".RARE METAL MATERIALS AND ENGINEERING 46.12(2017):3753-3759. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。