Microstructure Evolution During Solution Treatment and Its Effects on the Properties of Ni-Fe-Cr Alloy
文献类型：期刊论文
| 作者 | Chen Shenghu; Rong Lijian |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2018-03-11 |
| 卷号 | 54期号:3页码:385-392 |
| 关键词 | Ni-Fe-Cr alloy solution treatment carbide tensile property intergranular corrosion |
| ISSN号 | 0412-1961 |
| DOI | 10.11900/0412.1961.2017.00210 |
| 通讯作者 | Chen Shenghu(chensh@imr.ac.cn) |
| 英文摘要 | Ni-Fe-Cr alloys have been widely used for petrochemical, chemical and nuclear application due to their superior corrosion resistance and good workability. Nowadays, Ni-Fe-Cr alloys with higher strength are demanded for the engineering application. Increasing the carbon content could enhance the strength of Ni-Fe-Cr alloys due to the solid-solution strengthening effect of interstitial carbon atoms. However, an increase in the carbon content would promote the precipitation of carbides, which would reduce the corrosion resistance. In order to optimize the carbon content and determine the solution treatment, microstructure evolution during solution treatment and its effects on the properties of Ni-Fe-Cr alloys with different carbon content were investigated using OM and SEM. The results show that variation in carbon content affects the carbide dissolution and grain size during solution treatment, which affects the mechanical properties and intergranular corrosion susceptibility of Ni-Fe-Cr alloys. For the Ni-Fe-Cr alloy with carbon content of 0.010%, M23C6 carbides produced during the hot-working process do not exist after solution treatment at 950 degrees C. For the alloy with carbon content of 0.026%, M23C6 carbides are dissolved into the matrix when the solution temperature increases to 1000 degrees C. An increase in the carbon content from 0.010% to 0.026% results in an increased tensile strength and has slightly observable effect on the elongation. The alloys with the carbon content in the range of 0.010%similar to 0.026% have lower intergranular corrosion susceptibility. As the carbon content increases to 0.056%, M23C6 carbides could not be dissolved even at the solution temperature of 1050 degrees C, and inhomogenous grain-size distribution is observed. The presence of undissolved M23C6 carbide weakens the solid-solution strengthening effect of carbon atoms, and significantly increases the susceptibility to intergranular corrosion. |
| 资助项目 | National Natural Science Foundation of China[51401215] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000427121400004 |
| 出版者 | SCIENCE PRESS |
| 资助机构 | National Natural Science Foundation of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/127464]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Chen Shenghu |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Chen Shenghu,Rong Lijian. Microstructure Evolution During Solution Treatment and Its Effects on the Properties of Ni-Fe-Cr Alloy[J]. ACTA METALLURGICA SINICA,2018,54(3):385-392. |
| APA | Chen Shenghu,&Rong Lijian.(2018).Microstructure Evolution During Solution Treatment and Its Effects on the Properties of Ni-Fe-Cr Alloy.ACTA METALLURGICA SINICA,54(3),385-392. |
| MLA | Chen Shenghu,et al."Microstructure Evolution During Solution Treatment and Its Effects on the Properties of Ni-Fe-Cr Alloy".ACTA METALLURGICA SINICA 54.3(2018):385-392. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。