Preparation of CaO granules using the granulation method
文献类型：期刊论文
| 作者 | Zhang, Qi2; Wei, Yaowu2; Zhang, Tao2; Han, Bingqiang2; Liu, Kui1; Chen, Bo1 |
| 刊名 | ADVANCES IN APPLIED CERAMICS
 |
| 出版日期 | 2018 |
| 卷号 | 117期号:6页码:334-339 |
| 关键词 | CaO granules granulation method rotational speed hydration resistance |
| ISSN号 | 1743-6753 |
| DOI | 10.1080/17436753.2017.1422333 |
| 通讯作者 | Wei, Yaowu(weiyaowu@wust.edu.cn) |
| 英文摘要 | Improving the hydration resistance of CaO particle in manufacturing and application of free CaO-containing materials has practical significance. In this study, CaO granules was made from Ca(OH)(2) particles, which were fabricated by the granulation method. The results showed that the hydration resistance of the CaO granules which was prepared under 1700 r min(-1) was the best, the CaO granules was sintered well in calcination process, the shell of CaO granules was relatively dense, which improves the hydration resistance of CaO granules, and the rate of hydration weight increment was 0.58% after placed in the air for 20 days under a temperature of 10-14 degrees C and a relative humidity of 57-81%. |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:000434661800003 |
| 出版者 | TAYLOR & FRANCIS LTD |
| 源URL | [http://ir.imr.ac.cn/handle/321006/128195]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wei, Yaowu |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang, Peoples R China 2.Wuhan Univ Sci & Technol, State Key Lab Refractories & Met, 947 Heping Ave, Wuhan 430081, Hubei, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, Qi,Wei, Yaowu,Zhang, Tao,et al. Preparation of CaO granules using the granulation method[J]. ADVANCES IN APPLIED CERAMICS,2018,117(6):334-339. |
| APA | Zhang, Qi,Wei, Yaowu,Zhang, Tao,Han, Bingqiang,Liu, Kui,&Chen, Bo.(2018).Preparation of CaO granules using the granulation method.ADVANCES IN APPLIED CERAMICS,117(6),334-339. |
| MLA | Zhang, Qi,et al."Preparation of CaO granules using the granulation method".ADVANCES IN APPLIED CERAMICS 117.6(2018):334-339. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。