Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water
文献类型：期刊论文
| 作者 | Liao, Jiapeng1,2; Tan, Jibo2; Wu, Xinqiang2; Tang, Lichen3; Qian, Hao3; Xie, Yongcheng3 |
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2018-08-15 |
| 卷号 | 141页码:158-167 |
| 关键词 | Alloy SEM Fretting corrosion Corrosion fatigue High-temperature corrosion |
| ISSN号 | 0010-938X |
| DOI | 10.1016/j.corsci.2018.07.010 |
| 通讯作者 | Wu, Xinqiang(xqwu@imr.ac.cn) |
| 英文摘要 | Fretting corrosion fatigue behaviour of Alloy 690 was investigated in 285 degrees C pure water under different normal loads. With increasing the normal load applied, the fatigue life decreased, more severe surface damage and subsurface deformation were observed. The effects of normal loads on crack characteristics on the longitudinal sections across the fretting fatigue scars and corrosion fatigue fractures were examined. Possible influence of the normal loads on initiation and propagation mechanisms of the fretting corrosion fatigue cracks of Alloy 690 in high-temperature pure water are discussed. |
| 资助项目 | National Science and Technology Major Project[2017ZX06002003-004-002] ; National Natural Science Foundation of China[51671201] ; Key Programs of the Chinese Academy of Sciences (Research on the Development of Nuclear Power Materials and Service Security Technology)[ZDRW-CN-2017-1] ; Innovation Fund of Institute of Metal Research, Chinese Academy of Sciences[SCJJ-2013-ZD-02] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000441682000017 |
| 出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
| 资助机构 | National Science and Technology Major Project ; National Natural Science Foundation of China ; Key Programs of the Chinese Academy of Sciences (Research on the Development of Nuclear Power Materials and Service Security Technology) ; Innovation Fund of Institute of Metal Research, Chinese Academy of Sciences |
| 源URL | [http://ir.imr.ac.cn/handle/321006/129063]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wu, Xinqiang |
| 作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Anhui, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China 3.Shanghai Nucl Engn Res & Design Inst, Shanghai 200233, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liao, Jiapeng,Tan, Jibo,Wu, Xinqiang,et al. Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water[J]. CORROSION SCIENCE,2018,141:158-167. |
| APA | Liao, Jiapeng,Tan, Jibo,Wu, Xinqiang,Tang, Lichen,Qian, Hao,&Xie, Yongcheng.(2018).Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water.CORROSION SCIENCE,141,158-167. |
| MLA | Liao, Jiapeng,et al."Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water".CORROSION SCIENCE 141(2018):158-167. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。