Hot deformation characteristics and hot working window of as-cast large-tonnage GH3535 superalloy ingot

文献类型：期刊论文

作者Wang, Yao4,5; Wang, Junsong2; Dong, Jiasheng4; Li, Aimin3; Li, Zhijun1; Xie, Guang4,5; Lou, Langhong4
刊名JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
出版日期2018-12-01
卷号34期号:12页码:2439-2446
关键词Ni-base superalloy Dynamic recrystallization Hot working Large-tonnage ingot Processing map
ISSN号1005-0302
DOI10.1016/j.jmst.2018.04.001
通讯作者Dong, Jiasheng(djs@imr.ac.cn)
英文摘要Deformation characteristics and range of optimized hot working parameters of a 6.5 tons GH3535 super-alloy ingot with an average columnar grain size of over 1 mm in diameter were investigated. Axial compression experiments were performed in temperature range of 900-1240 degrees C and strain rate range of 0.001-30 s(-1) at a total strain of 0.8. The hot deformation activation energy of the experimental GH3535 alloy is calculated to be 483.22 kJ/mol. Furthermore, the deformation constitutive equation is established by the peak stresses obtained from the stress-strain curves under various conditions. The hot working window of the alloy ingot at a strain of 0.8 can be preliminarily discussed based on the deformed microstructures and processing maps. The optimized hot working window was thus determined at the strain of 0.95 for 6.5 tons GH3535 alloy ingot by the supplementary compression tests. A large-size GH3535 superalloy ring with a dimension of Phi 3010 mm x 410 mm was ultimately manufactured. (C) 2018 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
资助项目Strategic Priority Research Program of the Chinese Academy of Sciences[XDA02004210]
WOS研究方向Materials Science ; Metallurgy & Metallurgical Engineering
语种英语
WOS记录号WOS:000443274500029
出版者JOURNAL MATER SCI TECHNOL
资助机构Strategic Priority Research Program of the Chinese Academy of Sciences
源URL[http://ir.imr.ac.cn/handle/321006/129233]  
专题金属研究所_中国科学院金属研究所
通讯作者Dong, Jiasheng
作者单位1.Chinese Acad Sci, Shanghai Inst Appl Phys, Thorium Molten Salts Reactor Ctr, Shanghai 201800, Peoples R China
2.Harbin Engn Univ, Coll Mat Sci & Chem Engn, Harbin 150001, Heilongjiang, Peoples R China
3.Fushun Special Steel Shares Co Ltd, Ctr Technol, Fushun 113001, Peoples R China
4.Chinese Acad Sci, Inst Met Res, Superalloys Div, Shenyang 110016, Liaoning, Peoples R China
5.Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China
推荐引用方式
GB/T 7714		 Wang, Yao,Wang, Junsong,Dong, Jiasheng,et al. Hot deformation characteristics and hot working window of as-cast large-tonnage GH3535 superalloy ingot[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2018,34(12):2439-2446.
APA Wang, Yao.,Wang, Junsong.,Dong, Jiasheng.,Li, Aimin.,Li, Zhijun.,...&Lou, Langhong.(2018).Hot deformation characteristics and hot working window of as-cast large-tonnage GH3535 superalloy ingot.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,34(12),2439-2446.
MLA Wang, Yao,et al."Hot deformation characteristics and hot working window of as-cast large-tonnage GH3535 superalloy ingot".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 34.12(2018):2439-2446.

入库方式： OAI收割

来源：金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。