Influence of Deposition Temperature on Microstructures and Mechanical Properties of the Al-Cr-Si-N Coatings Deposited by HiPIMS Technique
文献类型：期刊论文
| 作者 | Wang Tiegang1; Li Baisong1; Zhang Jiaojiao1; Tang Kuanyu1; Liu Yanmei1; Jiang Sumeng2 |
| 刊名 | RARE METAL MATERIALS AND ENGINEERING
 |
| 出版日期 | 2018-08-01 |
| 卷号 | 47期号:8页码:2578-2584 |
| ISSN号 | 1002-185X |
| 关键词 | HiPIMS Al-Cr-Si-N coating deposition temperature mechanical property friction coefficient |
| 通讯作者 | Wang Tiegang(sytgwang@163.com) |
| 英文摘要 | Al-Cr-Si-N coating was prepared by high power pulsed magnetron sputtering (HiPIMS) technique at different deposition temperatures. The effects of deposition temperature on the composition, microstructure, mechanical properties and tribological properties of the coatings were investigated. The results show that as the deposition temperature rises from 100 degrees C to 350 degrees C, the microstructure of the coating begins to evolve from amorphous to nanocrystals, and the fcc-AlN phase appears at 300 degrees C. The smoothness and compactness of the coating are progressively improved. The adhesive strength increases gradually, reaches the maximum value of 77 N at 300 degrees C and sharply decreases to 25 N at 350 degrees C due to the serious glow etching effect. The hardness of the coating increases gradually and reaches a maximum of 19.4 GPa at 350 degrees C. No columnar crystals are found and the residual stress decreases from -0.8 GPa to about -0.4 GPa. |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
| WOS记录号 | WOS:000444219500048 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/129380]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wang Tiegang |
| 作者单位 | 1.Tianjin Univ Technol & Educ, Tianjin Key Lab High Speed Cutting & Precis Mfg, Tianjin 300222, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang Tiegang,Li Baisong,Zhang Jiaojiao,et al. Influence of Deposition Temperature on Microstructures and Mechanical Properties of the Al-Cr-Si-N Coatings Deposited by HiPIMS Technique[J]. RARE METAL MATERIALS AND ENGINEERING,2018,47(8):2578-2584. |
| APA | Wang Tiegang,Li Baisong,Zhang Jiaojiao,Tang Kuanyu,Liu Yanmei,&Jiang Sumeng.(2018).Influence of Deposition Temperature on Microstructures and Mechanical Properties of the Al-Cr-Si-N Coatings Deposited by HiPIMS Technique.RARE METAL MATERIALS AND ENGINEERING,47(8),2578-2584. |
| MLA | Wang Tiegang,et al."Influence of Deposition Temperature on Microstructures and Mechanical Properties of the Al-Cr-Si-N Coatings Deposited by HiPIMS Technique".RARE METAL MATERIALS AND ENGINEERING 47.8(2018):2578-2584. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。