Corrosion Behavior of Epoxy-Coated Rebar with Pinhole Defect in Seawater Concrete
文献类型：期刊论文
| 作者 | Mao, Yao-Zong1,2; Wei, Ying-Hua1; Zhao, Hong-Tao1; Lv, Chen-Xi1; Cao, Hai-Jiao1; Li, Jing1 |
| 刊名 | ACTA METALLURGICA SINICA-ENGLISH LETTERS
 |
| 出版日期 | 2018-11-01 |
| 卷号 | 31期号:11页码:1171-1182 |
| 关键词 | Corrosion Epoxy-coated rebar (ECR) Seawater concrete Pinhole defects |
| ISSN号 | 1006-7191 |
| DOI | 10.1007/s40195-018-0755-z |
| 通讯作者 | Wei, Ying-Hua(yhwei@imr.ac.cn) |
| 英文摘要 | Experiments were carried out to investigate the corrosion behavior of epoxy-coated rebar (ECR) with pinhole defect (diameter in hundreds of microns) immersed in the uncarbonated/carbonated simulated pore solution (SPS) of seawater concrete. Corrosion behavior was analyzed by electrochemical impedance spectroscopy. The composition and morphology of corrosion products were characterized by X-ray diffraction, energy-dispersive spectrometry and scanning electron microscopy. Meanwhile, oxide film produced by preheating before spray coating was investigated by X-ray photoelectron spectroscopy and Mott-Schottky technology. Results indicated that corrosion behavior of ECR with pinhole defect exhibited three stages when immersed in the uncarbonated/carbonated SPS. In the initial stage, steel in defect was passivated when exposed in the uncarbonated SPS and corroded when exposed in the carbonated SPS, due to competitive adsorption between chloride and hydroxyl ions. In the second stage, the oxide film under coating reconstituted (the thickness and defects density decreasing) in the uncarbonated SPS, which was caused by the synergy between high hydroxide and chloride activity, while in the carbonated SPS, crevice corrosion happened under the coating around pinhole, because of the different oxygen concentrations cell at the coating/steel interface. In the third stage, localized corrosion occurred under the coating around the pinhole in the uncarbonated SPS, which was probably induced by ion diffusion at the nano-scale coating/steel interface. The corrosion products adjacent to the defects were re-oxidized from FeCl(2)4H(2)O and Fe-2(OH)(3)Cl to Fe2O3H2O, and the corrosion area was expanded outward in the carbonated SPS. |
| 资助项目 | Strategic Precursor Research Program of the Chinese Academy of Sciences[XDA13040500] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000444031000005 |
| 出版者 | CHINESE ACAD SCIENCES, INST METAL RESEARCH |
| 资助机构 | Strategic Precursor Research Program of the Chinese Academy of Sciences |
| 源URL | [http://ir.imr.ac.cn/handle/321006/129422]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wei, Ying-Hua |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Anhui, Peoples R China |
| 推荐引用方式 GB/T 7714 | Mao, Yao-Zong,Wei, Ying-Hua,Zhao, Hong-Tao,et al. Corrosion Behavior of Epoxy-Coated Rebar with Pinhole Defect in Seawater Concrete[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2018,31(11):1171-1182. |
| APA | Mao, Yao-Zong,Wei, Ying-Hua,Zhao, Hong-Tao,Lv, Chen-Xi,Cao, Hai-Jiao,&Li, Jing.(2018).Corrosion Behavior of Epoxy-Coated Rebar with Pinhole Defect in Seawater Concrete.ACTA METALLURGICA SINICA-ENGLISH LETTERS,31(11),1171-1182. |
| MLA | Mao, Yao-Zong,et al."Corrosion Behavior of Epoxy-Coated Rebar with Pinhole Defect in Seawater Concrete".ACTA METALLURGICA SINICA-ENGLISH LETTERS 31.11(2018):1171-1182. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。