Very high cycle fatigue properties of bearing steel with different aluminum and sulfur content
文献类型：期刊论文
| 作者 | Yang, Chaoyun; Luan, Yikun1; Li, Dianzhong; Li, Yiyi |
| 刊名 | INTERNATIONAL JOURNAL OF FATIGUE
 |
| 出版日期 | 2018-11-01 |
| 卷号 | 116页码:396-408 |
| 关键词 | Very high cycle fatigue Bearing steel Aluminum content Sulfur content Crack initiation and propagation |
| ISSN号 | 0142-1123 |
| DOI | 10.1016/j.ijfatigue.2018.06.047 |
| 通讯作者 | Luan, Yikun(ykluan@imr.ac.cn) |
| 英文摘要 | This study aims to clarify the effects of aluminum and sulfur content on fatigue property together with corresponding crack initiation and propagation behavior of bearing steel in the very high cycle fatigue (VHCF) regime. For these purposes, ultrasonic tensile-compression fatigue tests were carried out on fatigue specimens with different directions extracted from bearing steel bars containing different aluminum and sulfur content. As a result, high aluminum content in bearing steel leads to worse fatigue property by forming a large collection area of Al2O3 particles. MnS inclusions can cause fatigue failure of low sulfur bearing steel at the 45-degree angle and contribute to fatigue anisotropy. However, there are no MnS inclusions to be found at crack initiation region of failed specimens with ultralow sulfur content. For the VHCF fracture of bearing steel, fracture surface can be simply divided into four different areas according to crack propagation path except fatigue source. The stress intensity factor at the periphery of fine granular area (FGA) Delta K-FGA can be regarded as the critical driving force for crack propagating through martensite laths. In addition, crack initiation and propagation are the result of mutual coordination and matching of the driving force Delta K, crack propagation speed and microstructure. Dislocations and precipitated carbides play an important role in the formation of FGA by helping form the corresponding nanoscale grain boundary. |
| 资助项目 | National Natural Science Foundation of China[U1708252] |
| WOS研究方向 | Engineering ; Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:000450377100038 |
| 出版者 | ELSEVIER SCI LTD |
| 资助机构 | National Natural Science Foundation of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/130291]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Luan, Yikun |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yang, Chaoyun,Luan, Yikun,Li, Dianzhong,et al. Very high cycle fatigue properties of bearing steel with different aluminum and sulfur content[J]. INTERNATIONAL JOURNAL OF FATIGUE,2018,116:396-408. |
| APA | Yang, Chaoyun,Luan, Yikun,Li, Dianzhong,&Li, Yiyi.(2018).Very high cycle fatigue properties of bearing steel with different aluminum and sulfur content.INTERNATIONAL JOURNAL OF FATIGUE,116,396-408. |
| MLA | Yang, Chaoyun,et al."Very high cycle fatigue properties of bearing steel with different aluminum and sulfur content".INTERNATIONAL JOURNAL OF FATIGUE 116(2018):396-408. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。