Influence of Aging Treatment on the Microstructure and High Temperature Mechanical Properties for 15Cr-15Ni Titanium-modified Austenitic Stainless Steel in 20% Cold-worked Condition
文献类型：期刊论文
| 作者 | Wang Zhinan1; Liang Tian1; Zhang Long1; Du Aibing2; Gao Ming1; Ma Yingche1; Liu Kui1 |
| 刊名 | RARE METAL MATERIALS AND ENGINEERING
 |
| 出版日期 | 2018-11-01 |
| 卷号 | 47期号:11页码:3504-3511 |
| 关键词 | titanium-stabilized 15Cr-15Ni austenitic stainless steel aging treatment high temperature tension Sigma phase |
| ISSN号 | 1002-185X |
| 通讯作者 | Liang Tian(tliang@imr.ac.cn) |
| 英文摘要 | Titanium-stabilized 15Cr-15Ni austenitic stainless steel in 20% cold-worked condition is considered as a promising candidate high temperature structural material for core components in liquid metal-cooled fast reactors (LMFR). Microstructure and high temperature mechanical properties of the as cold-worked alloy and the ones with different aging treatments were investigated by metallographic microscope, scanning and transmission electron microscope, and tensile testing machine. The results demonstrate that the recovery takes place when the alloy is aged at 550 degrees C for 336 h. The emergence of twins is attributed to dislocations movement. When the aging temperature increases to 650 and 750 degrees C, the amount of twins are reduced because of alloys' further recovery. Sigma phase precipitates from austenitic matrix along grain boundaries when alloys are aged at 650 similar to 750 degrees C for 336 h. The amount and size of Sigma phase increase with the increase in aging temperature. Because of the grain boundary strengthening, alloys aged at 550 degrees C have slightly higher yield strength and ultimate tensile strength than the as cold-worked alloy. The high temperature yield strength and ultimate tensile strength decrease significantly, while plasticity increases observably at the aging temperature of 650 and 750 degrees C. |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000452694200039 |
| 出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
| 源URL | [http://ir.imr.ac.cn/handle/321006/130730]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Liang Tian |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China 2.China Inst Atom Energy, Beijing 102413, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang Zhinan,Liang Tian,Zhang Long,et al. Influence of Aging Treatment on the Microstructure and High Temperature Mechanical Properties for 15Cr-15Ni Titanium-modified Austenitic Stainless Steel in 20% Cold-worked Condition[J]. RARE METAL MATERIALS AND ENGINEERING,2018,47(11):3504-3511. |
| APA | Wang Zhinan.,Liang Tian.,Zhang Long.,Du Aibing.,Gao Ming.,...&Liu Kui.(2018).Influence of Aging Treatment on the Microstructure and High Temperature Mechanical Properties for 15Cr-15Ni Titanium-modified Austenitic Stainless Steel in 20% Cold-worked Condition.RARE METAL MATERIALS AND ENGINEERING,47(11),3504-3511. |
| MLA | Wang Zhinan,et al."Influence of Aging Treatment on the Microstructure and High Temperature Mechanical Properties for 15Cr-15Ni Titanium-modified Austenitic Stainless Steel in 20% Cold-worked Condition".RARE METAL MATERIALS AND ENGINEERING 47.11(2018):3504-3511. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。