Microstructure and mechanical properties of h-BN/Yb4Si2O7N2 composites
文献类型：期刊论文
| 作者 | Chen, Juanjuan1,3; Chen, Jixin1; Zhang, Hao1,2; Hu, Minmin1,2; Li, Meishuan1 |
| 刊名 | JOURNAL OF ADVANCED CERAMICS
 |
| 出版日期 | 2018-12-01 |
| 卷号 | 7期号:4页码:317-324 |
| ISSN号 | 2226-4108 |
| 关键词 | h-BN Yb4Si2O7N2 composites microstructure mechanical properties machinability |
| DOI | 10.1007/s40145-018-0281-5 |
| 通讯作者 | Chen, Jixin(jxchen@imr.ac.cn) |
| 英文摘要 | A series of h-BN based composites with Yb4Si2O7N2 as a secondary phase were successfully synthesized by an in situ reaction hot pressing method. It was found that the relative density and room-temperature mechanical properties monotonically increased with increasing the content of Yb4Si2O7N2 from 20 to 50 vol%. When 50 vol% Yb4Si2O7N2 was introduced, the relative density of the composite reached 98.75%, and its flexural strength, compressive strength, fracture toughness, and hardness reached 338 +/- 10 MPa, 803 +/- 49 MPa, 2.06 +/- 0.06 MPam(1/2), and 2.69 +/- 0.10 GPa, respectively. The strengthening effect of Yb4Si2O7N2 was mainly attributed to its high modulus and high hardness. Fine microstructure was also advantageous to strength and could lead to more tortuous crack propagation paths and then improve the fracture toughness of the composites simultaneously. Meanwhile, the composites maintained good machinability. |
| 资助项目 | National Natural Science Foundation of China[50802099] ; National Natural Science Foundation of China[51072201] |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| 出版者 | SPRINGEROPEN |
| WOS记录号 | WOS:000453768100003 |
| 资助机构 | National Natural Science Foundation of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/130784]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Chen, Jixin |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang, Liaoning, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang, Liaoning, Peoples R China 3.Univ Chinese Acad Sci, Beijing, Peoples R China |
| 推荐引用方式 GB/T 7714 | Chen, Juanjuan,Chen, Jixin,Zhang, Hao,et al. Microstructure and mechanical properties of h-BN/Yb4Si2O7N2 composites[J]. JOURNAL OF ADVANCED CERAMICS,2018,7(4):317-324. |
| APA | Chen, Juanjuan,Chen, Jixin,Zhang, Hao,Hu, Minmin,&Li, Meishuan.(2018).Microstructure and mechanical properties of h-BN/Yb4Si2O7N2 composites.JOURNAL OF ADVANCED CERAMICS,7(4),317-324. |
| MLA | Chen, Juanjuan,et al."Microstructure and mechanical properties of h-BN/Yb4Si2O7N2 composites".JOURNAL OF ADVANCED CERAMICS 7.4(2018):317-324. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。