Effect of Bacillus flexus on the Degradation of Epoxy Resin Varnish Coating in Seawater
文献类型：期刊论文
| 作者 | Deng, Sanxi1; Wu, Jinyi1; Li, Yadong1; Wang, Gang1; Chai, Ke1; Yu, Aimin2; Liu, Fuchun3 |
| 刊名 | INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE
 |
| 出版日期 | 2019 |
| 卷号 | 14期号:1页码:315-328 |
| 关键词 | Epoxy resin varnish coating Bacillus flexus Degradation Electrochemical impedance spectroscopy Corrosion |
| ISSN号 | 1452-3981 |
| DOI | 10.20964/2019.01.64 |
| 通讯作者 | Chai, Ke(chaike888@sina.com) |
| 英文摘要 | Protective coatings have been being widely applied on the surface of metallic materials to protect against corrosion. However, there is still little known about the degradation of coatings caused by microbiological attack in seawater. As one of the most widespread species, Bacillus species are of great importance in the deterioration and degradation of materials. In this paper, the effect of Bacillus flexus on the degradation of an epoxy resin varnish coating in seawater was investigated. All the experiments were conducted in either sterile seawater or seawater containing Bacillus flexus. The electrochemical characteristics of the coatings in both kinds of seawater were monitored with electrochemical impedance spectroscopy (EIS). The reduction of the corrosion resistance of the coating exposed to seawater containing Bacillus flexus between 1 day of immersion and 19 days of immersion was evidently larger when compared with that in sterile seawater, which indicated that Bacillus flexus could remarkably decrease the corrosion resistance of the coating and potentially result in degradation of the coating. In addition, scanning electron microscopy (SEM) was employed for characterizing the surface morphology of the coatings before and after immersion. After 30 days of immersion, chalking traces and some tiny holes emerged on the surface of the coatings exposed to seawater containing Bacillus flexus, which was mainly ascribed to the biofilm formed by Bacillus flexus and their metabolic activities. The results demonstrated that the epoxy resin varnish coating was degraded by Bacillus flexus, which was further confirmed by the results obtained from Fourier transform infrared spectroscopy (FTIR). |
| 资助项目 | National Natural Science Foundation of China[51761011] ; National Natural Science Foundation of China[51261006] ; National Natural Science Foundation of China[51161007] ; National Natural Science Foundation of China[50761004] ; Hainan Provincial Natural Science Foundation of China[517064] ; National Basic Research Program of China[2014CB643304] |
| WOS研究方向 | Electrochemistry |
| 语种 | 英语 |
| WOS记录号 | WOS:000455046500026 |
| 出版者 | ESG |
| 资助机构 | National Natural Science Foundation of China ; Hainan Provincial Natural Science Foundation of China ; National Basic Research Program of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/131167]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Chai, Ke |
| 作者单位 | 1.Hainan Univ, Key Lab Adv Mat Trop Isl Resources, Minist Educ, Mat & Chem Engn Coll, Haikou 570228, Hainan, Peoples R China 2.Swinburne Univ Technol, Dept Chem & Biotechnol, Melbourne, Vic 3166, Australia 3.Chinese Acad Sci, Key Lab Nucl Mat & Safety Assessment, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Deng, Sanxi,Wu, Jinyi,Li, Yadong,et al. Effect of Bacillus flexus on the Degradation of Epoxy Resin Varnish Coating in Seawater[J]. INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,2019,14(1):315-328. |
| APA | Deng, Sanxi.,Wu, Jinyi.,Li, Yadong.,Wang, Gang.,Chai, Ke.,...&Liu, Fuchun.(2019).Effect of Bacillus flexus on the Degradation of Epoxy Resin Varnish Coating in Seawater.INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE,14(1),315-328. |
| MLA | Deng, Sanxi,et al."Effect of Bacillus flexus on the Degradation of Epoxy Resin Varnish Coating in Seawater".INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE 14.1(2019):315-328. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。