Characteristics and printability of K417G nickel-base alloy powder prepared by VIGA method
文献类型：期刊论文
| 作者 | Jia, Wuming1; Chen, Suiyuan1; Wei, Mingwei1; Liang, Jing1; Liu, Changsheng1; Li, Jinguo2 |
| 刊名 | POWDER METALLURGY
 |
| 出版日期 | 2019 |
| 卷号 | 62期号:1页码:30-37 |
| 关键词 | LAM blades K417G powder VIGA method powder characteristics |
| ISSN号 | 0032-5899 |
| DOI | 10.1080/00325899.2018.1546921 |
| 通讯作者 | Chen, Suiyuan(chensy@smm.neu.edu.cn) |
| 英文摘要 | Nickel-based K417G superalloy powder is the main material used in laser additive manufacturing (LAM) of aerospace engine turbine blades. In this study, K417G powder was prepared by the vacuum induction melting gas atomisation method (VIGA). Powder characteristics and microstructure were measured, and the properties of fabricated samples were studied. The results show that the powder mean particle size D-50 was 74 mu m, flowability was 16.6 s/50 g, apparent density was 4.78 g cm(-3), and the oxygen content of the powder was 0.015%. Powder and LAM sample microstructure consisted of gamma, gamma ', and carbide. The average microhardness was 410 HV, tensile strength was 1080 MPa, yield strength was 828 MPa and elongation was 13.52%. K417G superalloy powder prepared by VIGA method has potential for application in laser additive manufacturing. |
| 资助项目 | National Natural Science Foundation of Liaoning United fund[U1508213] ; National Key R&D Program of China[2016YFB1100201] ; Research and development plan for the future emerging industries in Shenyang[18-004-2-26] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000458410800004 |
| 出版者 | TAYLOR & FRANCIS LTD |
| 资助机构 | National Natural Science Foundation of Liaoning United fund ; National Key R&D Program of China ; Research and development plan for the future emerging industries in Shenyang |
| 源URL | [http://ir.imr.ac.cn/handle/321006/131537]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Chen, Suiyuan |
| 作者单位 | 1.Northeastern Univ, Key Lab Anisotropy & Texture Mat, Minist Educ, Key Lab Laser Applicat Technol Liaoning Prov,Sch, 11 Lane 3,WenHua Rd, Shenyang, Liaoning, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Jia, Wuming,Chen, Suiyuan,Wei, Mingwei,et al. Characteristics and printability of K417G nickel-base alloy powder prepared by VIGA method[J]. POWDER METALLURGY,2019,62(1):30-37. |
| APA | Jia, Wuming,Chen, Suiyuan,Wei, Mingwei,Liang, Jing,Liu, Changsheng,&Li, Jinguo.(2019).Characteristics and printability of K417G nickel-base alloy powder prepared by VIGA method.POWDER METALLURGY,62(1),30-37. |
| MLA | Jia, Wuming,et al."Characteristics and printability of K417G nickel-base alloy powder prepared by VIGA method".POWDER METALLURGY 62.1(2019):30-37. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。