The influence of niobium on the plastic deformation behaviors of 310s austenitic stainless steel weld metals at different temperatures
文献类型：期刊论文
| 作者 | Zhan, Xu1,2,3; Li, Dianzhong3; Li, Yiyi3; Lu, Shanping3 |
| 刊名 | MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
 |
| 出版日期 | 2019-01-16 |
| 卷号 | 743页码:648-655 |
| 关键词 | 310s austenitic weld metals Deformation twins Nb(C N) Temperature dependence Plasticity |
| ISSN号 | 0921-5093 |
| DOI | 10.1016/j.msea.2018.11.131 |
| 通讯作者 | Lu, Shanping(shplu@imr.ac.cn) |
| 英文摘要 | The deformation behaviors of 310s stainless steel weld metals (WMs) with different Nb contents are investigated under uniaxial tension at temperatures ranging from ambient temperature to 1000 degrees C. The results show that Nb effectively improves the strength of the WMs in the whole test temperatures range. The addition of Nb causes a change in the fractures of the WMs from intergranular brittle fractures to intragranular ductile fractures at elevated temperature. Hence, elemental Nb enhances the elevated temperature plasticity of the WMs. However, as the eutectic Nb(C, N) promotes the nucleation and propagation of the cracks, Nb decreases the elongation of the WMs at temperature below 700 degrees C. With the increase in the deformation temperature, the strength of the WMs decreases monotonously. However, the elongation of the WMs shows a nonmonotonic relationship with the temperatures. The deformation twins can occur at room temperature and improve the strength and elongation of the WMs. Meanwhile, the cracks nucleate around the eutectic Nb(C, N) at 1000 degrees C, leading to the minimum elongation of the Nb-bearing WMs in the whole test temperature range. The differential scanning calorimetry result suggests that the melting of the eutectic Nb(C, N) may be the dominant reason for the nucleation of the cracks and result in the reduction in the elongation of the Nb-bearing WM at 1000 degrees C. |
| 资助项目 | Research and Development of Nuclear Materials and Service Safety Assurance Technology[ZDRW-CN-2017-1] ; National Natural Science Foundation of China (NSFC)[51474203] |
| WOS研究方向 | Science & Technology - Other Topics ; Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000456891500073 |
| 出版者 | ELSEVIER SCIENCE SA |
| 资助机构 | Research and Development of Nuclear Materials and Service Safety Assurance Technology ; National Natural Science Foundation of China (NSFC) |
| 源URL | [http://ir.imr.ac.cn/handle/321006/131599]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Lu, Shanping |
| 作者单位 | 1.Chinese Acad Sci, Key Lab Nucl Mat & Safety Assessment, Inst Met Res, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China 3.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhan, Xu,Li, Dianzhong,Li, Yiyi,et al. The influence of niobium on the plastic deformation behaviors of 310s austenitic stainless steel weld metals at different temperatures[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2019,743:648-655. |
| APA | Zhan, Xu,Li, Dianzhong,Li, Yiyi,&Lu, Shanping.(2019).The influence of niobium on the plastic deformation behaviors of 310s austenitic stainless steel weld metals at different temperatures.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,743,648-655. |
| MLA | Zhan, Xu,et al."The influence of niobium on the plastic deformation behaviors of 310s austenitic stainless steel weld metals at different temperatures".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 743(2019):648-655. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。