Investigation on low-cycle fatigue behaviors of wrought superalloy GH4742 at room-temperature and 700 degrees C
文献类型：期刊论文
| 作者 | Kong, Wei-Wen1,2; Yuan, Chao1; Zhang, Bao-Ning1; Qin, He-Yong3; Zhao, Guang-Pu3 |
| 刊名 | MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
 |
| 出版日期 | 2019-03-28 |
| 卷号 | 751页码:226-236 |
| 关键词 | Wrought superalloy GH4742 Low-cycle fatigue Fatigue life Cycle hardening and softening Deformation mechanism |
| ISSN号 | 0921-5093 |
| DOI | 10.1016/j.msea.2019.02.075 |
| 通讯作者 | Yuan, Chao(ychao@imr.ac.en) |
| 英文摘要 | Low-cycle fatigue (LCF) behavior of wrought superalloy GH4742 was studied at room-temperature (RT) and 700 degrees C. Scanning electron microscope (SEM) and Transmission electron microscope (TEM) were used to study the development of cracks and deformation mechanism. An obvious decrease in fatigue life occurred as the temperature was increased from RT to 700 degrees C and as the total strain amplitude was raised from 0.5% to 1.0%. The Halford-Marrow relationship based on plastic strain energy density was used to predict the fatigue life, which is in good accordance with experimental data. At RT, for all investigated samples, initial cycle hardening is followed by gradual cycle softening especially at higher strain amplitude (Delta(t) >= 0.8%). Detailed TEM observation revealed that y' phase was sheared by dislocations. The shearing mechanism, reducing the ordering degree and diameter of gamma' phase, should be responsible for fatigue softening. Differently, at 700 degrees C, the tested samples exhibited continuous cycle hardening. A sharp drop in the number of stacking faults occurred. Lots of dislocation loops existed around tertiary gamma' phase and paired dislocations moved in secondary gamma' phase, indicating that Orowan and shearing mechanism have occurred. Fatigue cracks usually initiated from the surface. SEM investigation showed that the failure mode changed from transgranular to mixed transgranular and intergranular modes with increasing temperature. |
| WOS研究方向 | Science & Technology - Other Topics ; Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000463128800025 |
| 出版者 | ELSEVIER SCIENCE SA |
| 源URL | [http://ir.imr.ac.cn/handle/321006/132481]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Yuan, Chao |
| 作者单位 | 1.Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Anhui, Peoples R China 3.High Temp Mat Res Inst, Cent Iron & Steel Res Inst, Beijing 100081, Peoples R China |
| 推荐引用方式 GB/T 7714 | Kong, Wei-Wen,Yuan, Chao,Zhang, Bao-Ning,et al. Investigation on low-cycle fatigue behaviors of wrought superalloy GH4742 at room-temperature and 700 degrees C[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2019,751:226-236. |
| APA | Kong, Wei-Wen,Yuan, Chao,Zhang, Bao-Ning,Qin, He-Yong,&Zhao, Guang-Pu.(2019).Investigation on low-cycle fatigue behaviors of wrought superalloy GH4742 at room-temperature and 700 degrees C.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,751,226-236. |
| MLA | Kong, Wei-Wen,et al."Investigation on low-cycle fatigue behaviors of wrought superalloy GH4742 at room-temperature and 700 degrees C".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 751(2019):226-236. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。