Effect of Nanostructured Surface on the Corrosion Behavior of RAFM Steels
文献类型:期刊论文
作者 | Lu, Yanhong1; Zhang, Maolong1; Tang, Weibao1; Song, Yuanyuan2; Rong, Lijian2 |
刊名 | OXIDATION OF METALS |
出版日期 | 2019-04-01 |
卷号 | 91期号:3-4页码:495-510 |
ISSN号 | 0030-770X |
关键词 | Nanostructured surface RAFM Corrosion LBE alloy |
DOI | 10.1007/s11085-019-09895-0 |
通讯作者 | Rong, Lijian(ljrong@imr.ac.cn) |
英文摘要 | This study investigated the effect of a preformed nanostructured surface on the corrosion behavior of 9Cr2WVTa reduced activation ferritic/martensitic (RAFM) steel and 9Cr+AlSi steel (9Cr2WVTa with the 0.12 wt.% Al and 0.68 wt.% Si addition) at 700 degrees C in air and at 550 degrees C in liquid lead-bismuth eutectic (LBE) alloys. The nanostructured surface layer was fabricated by surface mechanical rolling treatment (SMRT). The results showed that the SMRT 9Cr+AlSi sample has a lower oxidation rate than the SMRT 9Cr2WVTa steel at 700 degrees C in air, due to the faster diffusion rates of Al, Cr and Si in the nanostructure and a higher diffusion driving force increased by Cr. The SMRT 9Cr+AlSi sample at 550 degrees C in oxygen-saturated LBE alloy also had a higher oxidation rate, due to the formation of Al and Si oxides in the internal oxide layer. [GRAPHICS] . |
资助项目 | Major Research Plan of the National Natural Science Foundation of China[91226204] ; Strategic Priority Research Program of the Chinese Academy of Science[XDA03010304] |
WOS研究方向 | Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | SPRINGER/PLENUM PUBLISHERS |
WOS记录号 | WOS:000462647800016 |
资助机构 | Major Research Plan of the National Natural Science Foundation of China ; Strategic Priority Research Program of the Chinese Academy of Science |
源URL | [http://ir.imr.ac.cn/handle/321006/132593] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Rong, Lijian |
作者单位 | 1.Shanghai Elect Nucl Power Equipment Co Ltd, Shanghai 201306, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China |
推荐引用方式 GB/T 7714 | Lu, Yanhong,Zhang, Maolong,Tang, Weibao,et al. Effect of Nanostructured Surface on the Corrosion Behavior of RAFM Steels[J]. OXIDATION OF METALS,2019,91(3-4):495-510. |
APA | Lu, Yanhong,Zhang, Maolong,Tang, Weibao,Song, Yuanyuan,&Rong, Lijian.(2019).Effect of Nanostructured Surface on the Corrosion Behavior of RAFM Steels.OXIDATION OF METALS,91(3-4),495-510. |
MLA | Lu, Yanhong,et al."Effect of Nanostructured Surface on the Corrosion Behavior of RAFM Steels".OXIDATION OF METALS 91.3-4(2019):495-510. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。