Thermal Ductility and Hot Cracking for 70 mm Thick Forge Plate and Rolling Plates of Nickel Alloy 690
文献类型：期刊论文
| 作者 | Jiang Yunlu2; Chen Huaining2; Wu Changzhong2; Chi Yunfei1 |
| 刊名 | RARE METAL MATERIALS AND ENGINEERING
 |
| 出版日期 | 2019-03-01 |
| 卷号 | 48期号:3页码:758-764 |
| 关键词 | nickel alloy 690 thermal ductility hot cracking |
| ISSN号 | 1002-185X |
| 通讯作者 | Chen Huaining(hnchen@imr.ac.cn) |
| 英文摘要 | The thermal ductility and hot cracking sensibility of the forge and the rolling plates with 70 mm in thickness were studied by optical microscope (OM), scanning electron microscope (SEM), and Gleeble 1500 thermal simulation equipment. The results show that the forge and the rolling plates both have excellent thermal ductility; the samples taken from surface position present higher thermal ductility than those taken from middle position of the same plate. During the heating process, the rolling plate has higher thermal ductility than the forge plate at the lower temperature. With the increase of the temperature, the forge plate is characterized by higher thermal ductility compared with the rolling plate. However, during the cooling process, the forge plate indicates higher thermal ductility than the rolling plate. The fracture position features more smoother morphology, even the melt phenomenon exists at some positions. Besides, high hot cracking sensitivity appears in both the forge and rolling nickel alloy 690. And the crack number and length increase with the applied strain increasing. |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000463845300009 |
| 出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
| 源URL | [http://ir.imr.ac.cn/handle/321006/132950]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Chen Huaining |
| 作者单位 | 1.Harbin Elect Corp Qinhuangdao Heavy Equipment Co, Qinhuangdao 066206, Peoples R China 2.Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Jiang Yunlu,Chen Huaining,Wu Changzhong,et al. Thermal Ductility and Hot Cracking for 70 mm Thick Forge Plate and Rolling Plates of Nickel Alloy 690[J]. RARE METAL MATERIALS AND ENGINEERING,2019,48(3):758-764. |
| APA | Jiang Yunlu,Chen Huaining,Wu Changzhong,&Chi Yunfei.(2019).Thermal Ductility and Hot Cracking for 70 mm Thick Forge Plate and Rolling Plates of Nickel Alloy 690.RARE METAL MATERIALS AND ENGINEERING,48(3),758-764. |
| MLA | Jiang Yunlu,et al."Thermal Ductility and Hot Cracking for 70 mm Thick Forge Plate and Rolling Plates of Nickel Alloy 690".RARE METAL MATERIALS AND ENGINEERING 48.3(2019):758-764. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。