Effects of nitrogen on precipitation and tensile behaviors of 25Cr-20Ni austenitic stainless steels at elevated temperatures
文献类型：期刊论文
| 作者 | Hu, Guodong1,2; Wang, Pei1,2; Li, Dianzhong1,2; Li, Yiyi1,2 |
| 刊名 | MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
 |
| 出版日期 | 2019-04-03 |
| 卷号 | 752页码:93-100 |
| 关键词 | Austenitic stainless steel Nitrogen High-temperature tensile property Precipitate Fracture mode |
| ISSN号 | 0921-5093 |
| DOI | 10.1016/j.msea.2019.03.004 |
| 通讯作者 | Wang, Pei(pwang@imr.ac.cn) |
| 英文摘要 | To understand the effects of nitrogen on precipitation and tensile behaviors at elevated temperatures, 25Cr-20Ni austenitic stainless steels with different nitrogen contents (0.065 wt %, 0.13 wt % and 0.17 wt %) were tensioned from room temperature to 1000 degrees C. Results show that the elongation and area reduction change differently with temperature increasing from 800 degrees C to 1000 degrees C, which are caused by different fracture modes. The necking concentrates in a small zone in the tensile samples of 0.17 wt % N steel, while the necking deformation occurs in all gauge length in specimens of other two steels. The local necking in 0.17 wt % N steel is induced by the enhanced recrystallization softening effect during tensile deformation. As the dislocation recovery are retarded by more solute nitrogen atoms and nitrides in 0.17 wt % N steel, the dislocation density difference between deformed grains and recrystallized grains turns larger, which results in a higher recrystallization rate and enhanced softening effect in further deformation. Additionally, the content of M23C6 precipitates unexpectedly increases with the increasing nitrogen after tensile test at 800 degrees C. This is because the increasing nitrogen promotes the formation of NbCrN in higher nitrogen steels during solution heat treatment, instead of Nb(C, N) in lower nitrogen steels. The precipitation of NbCrN releases carbon into austenitic matrix, leading to the acceleration of M23C6 precipitation during tensile test at 800 degrees C. |
| 资助项目 | Youth Innovation Promotion Association, Chinese Academy of Sciences[2013126] |
| WOS研究方向 | Science & Technology - Other Topics ; Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000464088200011 |
| 出版者 | ELSEVIER SCIENCE SA |
| 资助机构 | Youth Innovation Promotion Association, Chinese Academy of Sciences |
| 源URL | [http://ir.imr.ac.cn/handle/321006/132986]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wang, Pei |
| 作者单位 | 1.Chinese Acad Sci, Shenyang Natl Lab Mat Sci, Inst Met Res, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, 72 Wenhua Rd, Shenyang 110016, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Hu, Guodong,Wang, Pei,Li, Dianzhong,et al. Effects of nitrogen on precipitation and tensile behaviors of 25Cr-20Ni austenitic stainless steels at elevated temperatures[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2019,752:93-100. |
| APA | Hu, Guodong,Wang, Pei,Li, Dianzhong,&Li, Yiyi.(2019).Effects of nitrogen on precipitation and tensile behaviors of 25Cr-20Ni austenitic stainless steels at elevated temperatures.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,752,93-100. |
| MLA | Hu, Guodong,et al."Effects of nitrogen on precipitation and tensile behaviors of 25Cr-20Ni austenitic stainless steels at elevated temperatures".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 752(2019):93-100. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。