Influence of Cr content on high-temperature oxidation behaviour of arc sprayed Ni-Cr coatings
文献类型：期刊论文
| 作者 | Long, Weiyang3; Li, Jiahui3; Wu, Yuping1,3; Hong, Sheng2,3; Zhang, Jianfeng3; Qiao, Lei3 |
| 刊名 | MATERIALS AT HIGH TEMPERATURES
 |
| 出版日期 | 2019-05-04 |
| 卷号 | 36期号:3页码:187-194 |
| 关键词 | Arc spraying Ni-Cr coatings high-temperature oxidation protective scale |
| ISSN号 | 0960-3409 |
| DOI | 10.1080/09603409.2018.1503441 |
| 通讯作者 | Wu, Yuping(wuyuping@hhu.edu.cn) ; Hong, Sheng(hongsheng1988@126.com) |
| 英文摘要 | In this study, the high-temperature oxidation behaviour of arc-sprayed Ni-Cr coatings with high Cr contents of 30, 45 and 50 at.% was investigated in comparison with reference AISI 1020 steel. X-ray diffraction, scanning electron microscopy and energy dispersive spectroscopy were utilised to characterise the oxide scales. The oxidation resistance of the steel substrates was found to be enhanced after the application of the Ni-Cr coatings since the oxidation kinetics followed the parabolic law. In addition, the oxidation rate of Ni-50Cr coating was 56.5% lower than that of Ni-30Cr coating, indicating that the oxidation performance of coatings was improved with increasing Cr content. The oxide layers of Ni-Cr coating were found to be a double layer structure protecting the substrate from severely oxidation, which composed of a top layer of NiO and a basal layer of Cr2O3 and NiCr2O4. The surface of Ni-30Cr coating contained lots of multi-angle NiO crystals, while the surface of Ni-50Cr coating contained a dense Cr2O3 structure, suggesting that the growth of NiO crystals was limited due to the large amount of Cr-rich oxides. |
| 资助项目 | China Postdoctoral Science Foundation[2018T110435] ; China Postdoctoral Science Foundation[2016M590404] ; National Natural Science Foundation of China[51609067] ; National Natural Science Foundation of China[51579087] ; Opening Project of CAS Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences[2016NMSAKF03] ; Natural Science Foundation of Jiangsu Province of China[BK20150806] ; Opening Project of Material Corrosion and Protection Key Laboratory of Sichuan Province[2016CL08] |
| WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000472115600001 |
| 出版者 | TAYLOR & FRANCIS LTD |
| 资助机构 | China Postdoctoral Science Foundation ; National Natural Science Foundation of China ; Opening Project of CAS Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences ; Natural Science Foundation of Jiangsu Province of China ; Opening Project of Material Corrosion and Protection Key Laboratory of Sichuan Province |
| 源URL | [http://ir.imr.ac.cn/handle/321006/134081]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wu, Yuping; Hong, Sheng |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang, Liaoning, Peoples R China 2.Mat Corros & Protect Key Lab Sichuan Prov, Zigong, Peoples R China 3.Hohai Univ, Coll Mech & Mat, Nanjing, Jiangsu, Peoples R China |
| 推荐引用方式 GB/T 7714 | Long, Weiyang,Li, Jiahui,Wu, Yuping,et al. Influence of Cr content on high-temperature oxidation behaviour of arc sprayed Ni-Cr coatings[J]. MATERIALS AT HIGH TEMPERATURES,2019,36(3):187-194. |
| APA | Long, Weiyang,Li, Jiahui,Wu, Yuping,Hong, Sheng,Zhang, Jianfeng,&Qiao, Lei.(2019).Influence of Cr content on high-temperature oxidation behaviour of arc sprayed Ni-Cr coatings.MATERIALS AT HIGH TEMPERATURES,36(3),187-194. |
| MLA | Long, Weiyang,et al."Influence of Cr content on high-temperature oxidation behaviour of arc sprayed Ni-Cr coatings".MATERIALS AT HIGH TEMPERATURES 36.3(2019):187-194. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。