An Excellent Intrinsic Transparent Epoxy Resin with High Flame Retardancy: Synthesis, Characterization, and Properties
文献类型：期刊论文
| 作者 | Shao, Zhubao1,2; Yue, Weizheng1; Piao, Mingjun1; Ma, Jianying1; Lv, Xue1; Wang, Deyi2; Wang, Qi2,3 |
| 刊名 | MACROMOLECULAR MATERIALS AND ENGINEERING
 |
| 出版日期 | 2019-07-23 |
| 页码 | 10 |
| 关键词 | curing agents epoxy resins flame-retardant efficiency mechanical behavior |
| ISSN号 | 1438-7492 |
| DOI | 10.1002/mame.201900254 |
| 通讯作者 | Ma, Jianying(277533752@qq.com) ; Lv, Xue(pies112@126.com) |
| 英文摘要 | In this paper, a novel multifunctional, liquid, and colorless curing agent, namely DPTA, is prepared through diphenylphosphinic chloride (DPPC) and tetraethylenepentamine (TEPA). Different measurements confirm that the DPTA is prepared successfully and the cured DPTA-EPs simultaneously display excellent flame retardancy and transparency. The resulting DPTA-EP system reaches high optical transmittance up to 90% within the visible region. Meanwhile, the introduction of the flame-retardant groups in DPTA-EP does not deteriorate the mechanical behaviors compared with that of reference sample TEPA-EP. More importantly, with only 15 wt% DPTA addition, the resulting DPTA-EP with 1.6 mm passes UL-94 V-0 rating, and limiting oxygen index reaches 29.0%. Moreover, the peaks of heat release rate and total smoke production of DPTA-EP are largely reduced by 43.1% and 58.8%, respectively, further verifying the excellent smoke-suppression efficiency and flame retardancy. The analyses from both cone calorimeter (CC) and thermogravimetric (TG) results suggest that the satisfactory flame retardancy of cured DPTA-EP dominates in the gaseous phase. The earlier release of large amount of non-combustion gas and phosphorus containing groups improve the flame-retardant efficiency. |
| 资助项目 | National Natural Science Foundation of China[51703011] ; China Scholarship Council[201802335009] ; project of Jilin Provincial Department of Education[JJKH20191289KJ] |
| WOS研究方向 | Materials Science ; Polymer Science |
| 语种 | 英语 |
| WOS记录号 | WOS:000477440000001 |
| 出版者 | WILEY-V C H VERLAG GMBH |
| 资助机构 | National Natural Science Foundation of China ; China Scholarship Council ; project of Jilin Provincial Department of Education |
| 源URL | [http://ir.imr.ac.cn/handle/321006/134840]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Ma, Jianying; Lv, Xue |
| 作者单位 | 1.Changchun Univ Technol, Minist Educ, Engn Res Ctr Synthet Resin & Special Fiber, Changchun 130012, Jilin, Peoples R China 2.IMDEA Mat Inst, C Eric Kandel 2, Madrid 28906, Spain 3.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Shao, Zhubao,Yue, Weizheng,Piao, Mingjun,et al. An Excellent Intrinsic Transparent Epoxy Resin with High Flame Retardancy: Synthesis, Characterization, and Properties[J]. MACROMOLECULAR MATERIALS AND ENGINEERING,2019:10. |
| APA | Shao, Zhubao.,Yue, Weizheng.,Piao, Mingjun.,Ma, Jianying.,Lv, Xue.,...&Wang, Qi.(2019).An Excellent Intrinsic Transparent Epoxy Resin with High Flame Retardancy: Synthesis, Characterization, and Properties.MACROMOLECULAR MATERIALS AND ENGINEERING,10. |
| MLA | Shao, Zhubao,et al."An Excellent Intrinsic Transparent Epoxy Resin with High Flame Retardancy: Synthesis, Characterization, and Properties".MACROMOLECULAR MATERIALS AND ENGINEERING (2019):10. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。