Microstructure and Mechanical Performance of the DD98M-DD98M Single Crystal Superalloy Joints Brazed Using a Pd-Si Composite Filler

文献类型：期刊论文

作者Qin, Chunjie3; Xu, Haitao4; Zhou, Zhengqiang2; He, Yanming3,4; Lu, Chuanyang3,4; Gao, Ke3,4; Zheng, Wenjian3,4; Yang, Jianguo3,4; Wang, Donghong5; Sun, Yuan1
刊名METALS
出版日期2019-09-01
卷号9期号:9页码:14
关键词single crystal superalloy brazing microstructure shear strength
DOI10.3390/met9091001
通讯作者He, Yanming(heyanming@zjut.edu.cn) ; Sun, Yuan(yuansun@imr.ac.cn)
英文摘要In this work, the DD98M single crystal superalloys were brazed to themselves using a Pd-Si composite filler. The effect of brazing temperature and soaking time on the microstructure and mechanical behavior of the joints was studied. The microstructure and phase constitution in the joint were identified by the SEM and EDS analysis. The results indicated that the joint obtained was constituted by DD98M/zone 2/zone 1/zone 2/DD98M. The zone 1 was primarily made up of the Ni (Pd, Cr, Co) (s.s), Pd4Si, Pd (Ni, Ti, Al) (s.s) and Pd-rich Ni (Pd, Cr, Co) (s.s), while the zone 2 consisted of the Ni (Pd, Cr, Co) (s.s) and Al2Pd5. During the brazing process, increasing the brazing temperature strengthened the fluidity of the liquid filler, which was favorable to eliminating the solidified pores in the brazing seam. Furthermore, a higher brazing temperature would cause the phases in the zones 1 and 2 to be coarsened remarkably. When setting the brazing temperature to 1060 degrees C, extending the soaking time made the amount of Pd (Ni, Ti, Al) (s.s) decrease, whereas the amount of Pd4Si increased, because the peritectic reaction between the Pd (Ni, Ti, Al) (s.s) and remnant liquid filler was enhanced. Among the brazing process parameters under investigation, the maximum joint average shear strength obtained reached 338 MPa when the joint was brazed at 1060 degrees C for 30 min. A ductile fracture mode happened during the shear tests under a joining condition. The work performed can provide valuable data to design the single crystal superalloy brazed joint.
资助项目National Natural Science Foundation of China[51405439] ; National Natural Science Foundation of China[51705461] ; Natural Science Foundation of Zhejiang Province[LY17E050019]
WOS研究方向Materials Science ; Metallurgy & Metallurgical Engineering
语种英语
出版者MDPI
WOS记录号WOS:000489129800087
资助机构National Natural Science Foundation of China ; Natural Science Foundation of Zhejiang Province
源URL[http://ir.imr.ac.cn/handle/321006/135638]  
专题金属研究所_中国科学院金属研究所
通讯作者He, Yanming; Sun, Yuan
作者单位1.Chinese Acad Sci, Inst Met Res, Dept Superalloy, Shenyang 110016, Peoples R China
2.Zhejiang Prov Elect Power Sci & Res Inst, Hangzhou 310014, Zhejiang, Peoples R China
3.Zhejiang Univ Technol, Coll Mech Engn, Hangzhou 310014, Zhejiang, Peoples R China
4.Zhejiang Univ Technol, Inst Proc Equipment & Control Engn, Hangzhou 310014, Zhejiang, Peoples R China
5.Zhejiang Univ Technol, Sch Chem Engn, Hangzhou 310014, Zhejiang, Peoples R China
推荐引用方式
GB/T 7714		 Qin, Chunjie,Xu, Haitao,Zhou, Zhengqiang,et al. Microstructure and Mechanical Performance of the DD98M-DD98M Single Crystal Superalloy Joints Brazed Using a Pd-Si Composite Filler[J]. METALS,2019,9(9):14.
APA Qin, Chunjie.,Xu, Haitao.,Zhou, Zhengqiang.,He, Yanming.,Lu, Chuanyang.,...&Gao, Zengliang.(2019).Microstructure and Mechanical Performance of the DD98M-DD98M Single Crystal Superalloy Joints Brazed Using a Pd-Si Composite Filler.METALS,9(9),14.
MLA Qin, Chunjie,et al."Microstructure and Mechanical Performance of the DD98M-DD98M Single Crystal Superalloy Joints Brazed Using a Pd-Si Composite Filler".METALS 9.9(2019):14.

入库方式： OAI收割

来源：金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。