Seed Preparation and Orientation Control of PST Crystals of Ti-47Al Alloy
文献类型：期刊论文
| 作者 | Jin Hao1,2; Jia Qing1; Liu Ronghua1; Xian Quangang1; Cui Yuyou1; Xu Dongsheng1; Yang Rui1 |
| 刊名 | ACTA METALLURGICA SINICA
 |
| 出版日期 | 2019-12-11 |
| 卷号 | 55期号:12页码:1519-1526 |
| 关键词 | TiAl alloy polysynthetically twinned crystal seed technique directional solidification optical floating zone furnace |
| ISSN号 | 0412-1961 |
| DOI | 10.11900/0412.1961.2019.00138 |
| 通讯作者 | Yang Rui(ryang@imr.ac.cn) |
| 英文摘要 | Button ingots were prepared by arc melting and feed bars for directional solidification were prepared by optimized drop casting technique. The Ti-43Al-3Si directionally solidified bars with lamellar boundaries perpendicular to the growth direction were prepared at the growth rate of 180 mm/h in an optical floating zone furnace. Cylindrical sections were cut from these perpendicular lamellae with appropriate direction and then fixed on polycrystalline TiAl bars by mechanical setting method to serve as the initial seeds. The ultimate Ti-43Al-3Si seeds with parallel lamellar microstructure were successfully prepared from these initial seeds at the growth rate of 5 mm/h. To avoid the nucleation of stray grains, drop-cast bars with the shape of frustum of a cone were used for the preparation of ultimate seeds. At the growth rates of 5 and 180 mm/h, the primary phase of Ti-43Al-3Si alloy was always the a phase. Polysynthetically twinned (PST) crystals of Ti-47Al alloy were obtained from the Ti-43Al-3Si ultimate seeds and the seeding process was studied by microscopic analysis. Lamellar microstructure of the seed kept stable and recrystallization of the seed was not found. Lamellar orientation of Ti-47Al PST crystals was successfully controlled by the ultimate Ti-43Al-3Si seed. |
| 资助项目 | National Natural Science Foundation of China[51701209] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000497774900005 |
| 出版者 | SCIENCE PRESS |
| 资助机构 | National Natural Science Foundation of China |
| 源URL | [http://ir.imr.ac.cn/handle/321006/136047]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Yang Rui |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Jin Hao,Jia Qing,Liu Ronghua,et al. Seed Preparation and Orientation Control of PST Crystals of Ti-47Al Alloy[J]. ACTA METALLURGICA SINICA,2019,55(12):1519-1526. |
| APA | Jin Hao.,Jia Qing.,Liu Ronghua.,Xian Quangang.,Cui Yuyou.,...&Yang Rui.(2019).Seed Preparation and Orientation Control of PST Crystals of Ti-47Al Alloy.ACTA METALLURGICA SINICA,55(12),1519-1526. |
| MLA | Jin Hao,et al."Seed Preparation and Orientation Control of PST Crystals of Ti-47Al Alloy".ACTA METALLURGICA SINICA 55.12(2019):1519-1526. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。