Influence of Mo contents on the tribological properties of CrMoN/MoS2 coatings at 25-700 degrees C
文献类型：期刊论文
| 作者 | Lu, Cheng2,3; Jia, Junhong2,4; Fu, Yingying2; Yi, Gewen2; Feng, Xiaochun2,3; Yang, Jingjing2,3; Zhou, Qi2; Xie, Erqing1; Sun, Yuan5 |
| 刊名 | SURFACE & COATINGS TECHNOLOGY
 |
| 出版日期 | 2019 |
| 卷号 | 378页码:8 |
| 关键词 | CrMoN/MoS2 composite coating Mechanical property Tribological property High-temperature |
| ISSN号 | 0257-8972 |
| DOI | 10.1016/j.surfcoat.2019.125072 |
| 通讯作者 | Jia, Junhong(jhjia@licp.cas.cn) ; Fu, Yingying(yingyingf@licp.cas.cn) |
| 英文摘要 | CrMoN/MoS2 coatings with different Mo contents were fabricated by magnetron sputtering technique. The microstructure, mechanical and wear properties at elevated temperatures of coatings were investigated. The results show that the coating (Mo: 18.5 at.%) exhibited moderate hardness and high adhesion strength, which was primarily due to the effect of solid solution enhancement. Almost all of the Mo added composite coatings demonstrated good wear resistance performance with low wear rates of 10(-6) mm(3) (N m)(-1) magnitude although they had high friction coefficients at RT and 500 degrees C. Particularly, the coating (Mo: 18.5 at.%) exhibited excellent wear resistance property at 700 degrees C, which was attributed to the outstanding adhesive strength of coating and lubrication of Cr2O3, MoO2 and MoO3. |
| 资助项目 | National Natural Science Foundation of China[51575505] ; National Natural Science Foundation of China[51675508] ; CAS Light of West China Program ; State Key Laboratory of Solid Lubrication[LSL-1610] |
| WOS研究方向 | Materials Science ; Physics |
| 语种 | 英语 |
| WOS记录号 | WOS:000503100800085 |
| 出版者 | ELSEVIER SCIENCE SA |
| 资助机构 | National Natural Science Foundation of China ; CAS Light of West China Program ; State Key Laboratory of Solid Lubrication |
| 源URL | [http://ir.imr.ac.cn/handle/321006/136545]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Jia, Junhong; Fu, Yingying |
| 作者单位 | 1.Lanzhou Univ, Sch Phys Sci & Technol, Lanzhou 730000, Gansu, Peoples R China 2.Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou 730000, Gansu, Peoples R China 3.Univ Chinese Acad Sci, Ctr Mat Sci & Optoelect Engn, Beijing 100049, Peoples R China 4.Shanxi Univ Sci & Technol, Coll Mech & Elect Engn, Xian 710021, Shaanxi, Peoples R China 5.Chinese Acad Sci, Inst Met Res, Dept Superalloys, Shenyang 110016, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Lu, Cheng,Jia, Junhong,Fu, Yingying,et al. Influence of Mo contents on the tribological properties of CrMoN/MoS2 coatings at 25-700 degrees C[J]. SURFACE & COATINGS TECHNOLOGY,2019,378:8. |
| APA | Lu, Cheng.,Jia, Junhong.,Fu, Yingying.,Yi, Gewen.,Feng, Xiaochun.,...&Sun, Yuan.(2019).Influence of Mo contents on the tribological properties of CrMoN/MoS2 coatings at 25-700 degrees C.SURFACE & COATINGS TECHNOLOGY,378,8. |
| MLA | Lu, Cheng,et al."Influence of Mo contents on the tribological properties of CrMoN/MoS2 coatings at 25-700 degrees C".SURFACE & COATINGS TECHNOLOGY 378(2019):8. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。