Hot Deformation Behavior and Processing Map of a Cu-Bearing 2205 Duplex Stainless Steel
文献类型：期刊论文
| 作者 | Xi, Tong; Yin, Lu; Yang, Chun-Guang; Yang, Ke |
| 刊名 | ACTA METALLURGICA SINICA-ENGLISH LETTERS
 |
| 出版日期 | 2019-12-01 |
| 卷号 | 32期号:12页码:1537-1548 |
| 关键词 | Cu-bearing duplex stainless steel Hot deformation Processing map Dynamic recrystallization Dynamic recovery |
| ISSN号 | 1006-7191 |
| DOI | 10.1007/s40195-019-00910-6 |
| 通讯作者 | Yang, Chun-Guang(cgyang@imr.ac.cn) ; Yang, Ke(kyang@imr.ac.cn) |
| 英文摘要 | The hot deformation behavior and processing map of Cu-bearing 2205 duplex stainless steel (2205-Cu DSS) were investigated at temperatures of 950-1150 degrees C and strain rates of 0.01-10 s(-1). The effects of Cu addition and different deformation parameters on deformation behavior were, respectively, characterized by analyzing flow curves, constitutive equations and microstructures. The results indicated that the shapes of flow curves strongly depended on the volume fraction of two phases. When deformed at low strain rate, DRV in ferrite was prompted with increase in the temperature and was further developed to continuous DRX. At high strain rate, flow localization preferentially occurred in ferrite at low deformation temperature due to the strain partitioning and relatively less fraction of ferrite. The activation energy for 2205-Cu DSS was 452 kJ/mol and was found to connect with the variation of strain, strain rate and deformation temperature. The optimum hot deformation parameters for 2205-Cu DSS were obtained in the temperature range of 1100-1150 degrees C and strain rate range of 0.1-1 s(-1) with a peak power dissipation efficiency of 41%. Flow localization was the main way to lead to flow instability. Meanwhile, the Cu-rich precipitates were generated within a few ferrite grains when deformed at temperature lower than 1000 degrees C. The interaction between dislocations and Cu-rich precipitates at high strain rate, as well as the limited DRV in ferrite and DRX in austenite, contributed to the complex microstructure and flow behavior. |
| 资助项目 | National Key Research and Development Program of China[2016YFB0300205] ; National Natural Science Foundation of China[51501188] ; National Natural Science Foundation of China[51771199] ; State Key Program of National Natural Science of China[51631009] ; Shenzhen-Hong Kong Technology Cooperation Funding Scheme[SGLH20150213143207910] ; Shenzhen Science and Technology Research Funding[JCYJ20160608153641020] |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000495116000011 |
| 出版者 | CHINESE ACAD SCIENCES, INST METAL RESEARCH |
| 资助机构 | National Key Research and Development Program of China ; National Natural Science Foundation of China ; State Key Program of National Natural Science of China ; Shenzhen-Hong Kong Technology Cooperation Funding Scheme ; Shenzhen Science and Technology Research Funding |
| 源URL | [http://ir.imr.ac.cn/handle/321006/136836]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Yang, Chun-Guang; Yang, Ke |
| 作者单位 | Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China |
| 推荐引用方式 GB/T 7714 | Xi, Tong,Yin, Lu,Yang, Chun-Guang,et al. Hot Deformation Behavior and Processing Map of a Cu-Bearing 2205 Duplex Stainless Steel[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2019,32(12):1537-1548. |
| APA | Xi, Tong,Yin, Lu,Yang, Chun-Guang,&Yang, Ke.(2019).Hot Deformation Behavior and Processing Map of a Cu-Bearing 2205 Duplex Stainless Steel.ACTA METALLURGICA SINICA-ENGLISH LETTERS,32(12),1537-1548. |
| MLA | Xi, Tong,et al."Hot Deformation Behavior and Processing Map of a Cu-Bearing 2205 Duplex Stainless Steel".ACTA METALLURGICA SINICA-ENGLISH LETTERS 32.12(2019):1537-1548. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。