High-Speed Friction Stir Welding of T6-Treated B4Cp/6061Al Composite
文献类型：期刊论文
| 作者 | Li, Y. Z.1; Zan, Y. N.2,3; Wang, Q. Z.1; Xiao, B. L.2; Ma, Z. Y.2 |
| 刊名 | ACTA METALLURGICA SINICA-ENGLISH LETTERS
 |
| 出版日期 | 2020 |
| 卷号 | 33期号:1页码:67-74 |
| 关键词 | Metal-matrix composites Microstructures Mechanical properties Friction stir welding High-speed welding |
| ISSN号 | 1006-7191 |
| DOI | 10.1007/s40195-019-00932-0 |
| 通讯作者 | Wang, Q. Z.(qzhwang@imr.ac.cn) ; Ma, Z. Y.(zyma@imr.ac.cn) |
| 英文摘要 | T6-treated 20 wt% B4Cp/6061Al sheets were joined under welding speeds of 400-1200 mm/min by friction stir welding (FSW) with a threaded cermet pin. The macro-defect-free FSW joints could be achieved at high welding speeds up to 1200 mm/min, but larger plunge depth was required at the welding speeds of 800 and 1200 mm/min to eliminate the tunnel defect. In the nugget zone (NZ) of the joints, the B4C particles were broken up and uniformly redistributed. The NZ exhibited lower hardness than the base metal (BM), and the hardness value almost did not change with increasing welding speed, attributable to the dissolution of precipitates. Compared with the BM, the joints showed lower tensile strength. As the welding speed increased from 400 to 800 mm/min, the joint efficiencies were nearly the same and up to ~ 73%. When the welding speed increased up to 1200 mm/min, the tensile strength significantly decreased, due to the occurrence of kissing bond defect at the bottom of the NZ. With increasing welding speed, the fracture location of the joints transferred gradually from the heat-affected zone to the NZ due to the kissing bond defects. |
| WOS研究方向 | Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| WOS记录号 | WOS:000512013800006 |
| 出版者 | CHINESE ACAD SCIENCES, INST METAL RESEARCH |
| 源URL | [http://ir.imr.ac.cn/handle/321006/137434]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Wang, Q. Z.; Ma, Z. Y. |
| 作者单位 | 1.Chinese Acad Sci, Inst Met Res, Key Lab Nucl Mat & Safety Assessment, 72 Wenhua Rd, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Peoples R China 3.Univ Sci & Technol China, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Li, Y. Z.,Zan, Y. N.,Wang, Q. Z.,et al. High-Speed Friction Stir Welding of T6-Treated B4Cp/6061Al Composite[J]. ACTA METALLURGICA SINICA-ENGLISH LETTERS,2020,33(1):67-74. |
| APA | Li, Y. Z.,Zan, Y. N.,Wang, Q. Z.,Xiao, B. L.,&Ma, Z. Y..(2020).High-Speed Friction Stir Welding of T6-Treated B4Cp/6061Al Composite.ACTA METALLURGICA SINICA-ENGLISH LETTERS,33(1),67-74. |
| MLA | Li, Y. Z.,et al."High-Speed Friction Stir Welding of T6-Treated B4Cp/6061Al Composite".ACTA METALLURGICA SINICA-ENGLISH LETTERS 33.1(2020):67-74. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。