The Effect of Lath Martensite Microstructures on the Strength of Medium-Carbon Low-Alloy Steel
文献类型：期刊论文
| 作者 | Sun, Chen1,2; Fu, Paixian2; Liu, Hongwei2; Liu, Hanghang2; Du, Ningyu1,2; Cao, Yanfei2 |
| 刊名 | CRYSTALS
 |
| 出版日期 | 2020-03-01 |
| 卷号 | 10期号:3页码:12 |
| 关键词 | medium-carbon low-alloy steel lath martensite effective grain size strength carbon content |
| ISSN号 | 2073-4352 |
| DOI | 10.3390/cryst10030232 |
| 通讯作者 | Fu, Paixian(pxfu@imr.ac.cn) ; Cao, Yanfei(yfcao10s@imr.ac.cn) |
| 英文摘要 | Different austenitizing temperatures were used to obtain medium-carbon low-alloy (MCLA) martensitic steels with different lath martensite microstructures. The hierarchical microstructures of lath martensite were investigated by optical microscopy (OM), electron backscattering diffraction (EBSD), and transmission electron microscopy (TEM). The results show that with increasing the austenitizing temperature, the prior austenite grain size and block size increased, while the lath width decreased. Further, the yield strength and tensile strength increased due to the enhancement of the grain boundary strengthening. The fitting results reveal that only the relationship between lath width and strength followed the Hall-Petch formula of. Hence, we propose that lath width acts as the effective grain size (EGS) of strength in MCLA steel. In addition, the carbon content had a significant effect on the EGS of martensitic strength. In steels with lower carbon content, block size acted as the EGS, while, in steels with higher carbon content, the EGS changed to lath width. The effect of the Cottrell atmosphere around boundaries may be responsible for this change. |
| 资助项目 | National Natural Science Foundation of China[51701225] ; Project to Strengthen Industrial Development at the Grass-roots Level[TC190A4DA/35] ; Independent & Controllable Manufacturing of Advanced Bearing ; Innovation project of the cutting-edge basic research and key technology by SYNL[L2019R36] ; Young Talent Project by SYNL[L2019F33] ; China Postdoctoral Science Foundation[2019M661153] |
| WOS研究方向 | Crystallography ; Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:000523512100031 |
| 出版者 | MDPI |
| 资助机构 | National Natural Science Foundation of China ; Project to Strengthen Industrial Development at the Grass-roots Level ; Independent & Controllable Manufacturing of Advanced Bearing ; Innovation project of the cutting-edge basic research and key technology by SYNL ; Young Talent Project by SYNL ; China Postdoctoral Science Foundation |
| 源URL | [http://ir.imr.ac.cn/handle/321006/137941]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 通讯作者 | Fu, Paixian; Cao, Yanfei |
| 作者单位 | 1.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China 2.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China |
| 推荐引用方式 GB/T 7714 | Sun, Chen,Fu, Paixian,Liu, Hongwei,et al. The Effect of Lath Martensite Microstructures on the Strength of Medium-Carbon Low-Alloy Steel[J]. CRYSTALS,2020,10(3):12. |
| APA | Sun, Chen,Fu, Paixian,Liu, Hongwei,Liu, Hanghang,Du, Ningyu,&Cao, Yanfei.(2020).The Effect of Lath Martensite Microstructures on the Strength of Medium-Carbon Low-Alloy Steel.CRYSTALS,10(3),12. |
| MLA | Sun, Chen,et al."The Effect of Lath Martensite Microstructures on the Strength of Medium-Carbon Low-Alloy Steel".CRYSTALS 10.3(2020):12. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。