Effect of Ta on microstructural evolution of NiCrAlYSi coated Ni-base single crystal superalloys
文献类型:期刊论文
作者 | Yin, Bin1,2; Xie, Guang1; Lou, Langhong1; Zhang, Jian1 |
刊名 | JOURNAL OF ALLOYS AND COMPOUNDS |
出版日期 | 2020-07-15 |
卷号 | 829页码:14 |
ISSN号 | 0925-8388 |
关键词 | Single crystal superalloys NiCrAlYSi coating Ta Secondary reaction zone (SRZ) Rafting |
DOI | 10.1016/j.jallcom.2020.154440 |
通讯作者 | Xie, Guang(gxie@imr.ac.cn) |
英文摘要 | The effect of Ta on microstructural evolution of NiCrAlYSi coated Ni-base single crystal superalloys at 1000 degrees C and 1100 degrees C has been investigated. Interdiffusion occurs between the NiCrAlYSi coating and the substrate, leading to the formation of inter-diffusion zone (IDZ) and secondary reaction zone (SRZ). After exposure at 1000 degrees C for 100 h, the initial gamma/gamma' transforms to gamma' phases in the IDZ, and SRZ with sigma and mu topologically close-packed (TCP) phases is formed primarily due to the inward diffusion of Al. Different behavior of SRZ formation in the alloys with various Ta content can be observed after exposure at 1000 degrees C, which highlights the potency of Ta addition in promoting SRZ formation. This may be ascribed to the fact that Ta promotes the precipitation of TCP phases. After exposure at 1100 degrees C for 100 h, the initial gamma/gamma' transforms to y layer and coarse gamma' phases in the IDZ, and no SRZ can be found. The formation of IDZ is significantly suppressed by Ta addition, which may be related to the retardation of interdiffusion between the coating and the substrate due to the increased gamma' volume fraction. Furthermore, gamma' rafting parallel to and/or perpendicular to the coating/substrate interface in the substrate beneath IDZ are found in the alloys after exposure at 1000 degrees C and 1100 degrees C. Microstructural observation shows that Ta has a potent influence on the development of perpendicular gamma' rafting. The mechanism of parallel gamma' rafting and perpendicular gamma' rafting has been discussed, respectively. (C) 2020 Elsevier B.V. All rights reserved. |
资助项目 | National Natural Science Foundation of China[51771204] ; National Natural Science Foundation of China[U1732131] ; National Natural Science Foundation of China[51631008] ; National Natural Science Foundation of China[91860201] ; National Natural Science Foundation of China[51911530154] |
WOS研究方向 | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | ELSEVIER SCIENCE SA |
WOS记录号 | WOS:000523555300039 |
资助机构 | National Natural Science Foundation of China |
源URL | [http://ir.imr.ac.cn/handle/321006/137994] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Xie, Guang |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Superalloys Div, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China |
推荐引用方式 GB/T 7714 | Yin, Bin,Xie, Guang,Lou, Langhong,et al. Effect of Ta on microstructural evolution of NiCrAlYSi coated Ni-base single crystal superalloys[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2020,829:14. |
APA | Yin, Bin,Xie, Guang,Lou, Langhong,&Zhang, Jian.(2020).Effect of Ta on microstructural evolution of NiCrAlYSi coated Ni-base single crystal superalloys.JOURNAL OF ALLOYS AND COMPOUNDS,829,14. |
MLA | Yin, Bin,et al."Effect of Ta on microstructural evolution of NiCrAlYSi coated Ni-base single crystal superalloys".JOURNAL OF ALLOYS AND COMPOUNDS 829(2020):14. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。